Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 5140H plate,AISI 5140H Round Bar,AISI 5140H forgings,AISI 5140H suppliers, AISI 5140H Stock,AISI 5140H sheet, AISI 5140H flat bar, AISI 5140H pipe,AISI 5140H tube,AISI 5140H mould,AISI 5140H round ingot,AISI 5140H cold-rolled steel,AISI 5140H coil,AISI 5140H strap steel,AISI 5140H hot-rolled steel,AISI 5140H medium plate, AISI 5140H heavy plate,AISI 5140H shapped bar,AISI 5140H hexahedral bar,AISI 5140H,AISI 5140H slab ingot,AISI 5140H slab,AISI 5140H price,AISI 5140H square bar,AISI 5140H square steel,AISI 5140H wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 5140H.

Current Location:Home » Products » Alloy steel » AISI 5140H

Product category

AISI 5140H

Data Table for:Products: Alloy steel:AISI 5140H

AISI 5140H properties and heat treatment forged piece, Including AISI 5140H application and specifications, We have all specifications,Including AISI 5140H steel plate, AISI 5140H sheet, AISI 5140H square steel, AISI 5140H flat bar,AISI 5140H round bar,AISI 5140H forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 5140H has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 5140H and Standards

Designations
France: AFNOR 45 C 2
Germany: DIN 1.7006
United States: ASTM A304 , SAE J1268 , UNS H51400

Chemical Composition
Element
Weight %
C
 0.37-0.44 
Mn
 0.60-1.00 
Cr
 0.60-1.00 
P
 0.035 
S
 0.040 
Si
 0.15-0.30 
 Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Tensile Strength (Mpa)
570 
25 
annealed at 830°C 
Yield Strength (Mpa)
295 
Elongation (%)
28.6 
Reduction in Area (%)
57 
Hardness (HB)
167 
25 
annealed at 830°C
Thermal Properties
Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
12.6 
20-200 
 
Thermal Conductivity (W/m-K)
44.6 
100 
 
Specific Heat (J/kg-K)
452 
20-100
 
Electric Properties
 
Properties
 Conditions 
T (°C)
Treatment
Electric Resistivity (10-9W-m)
228 
20
 



Machining performance

Download AISI 5140H the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.