Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 50B46 plate,AISI 50B46 Round Bar,AISI 50B46 forgings,AISI 50B46 suppliers, AISI 50B46 Stock,AISI 50B46 sheet, AISI 50B46 flat bar, AISI 50B46 pipe,AISI 50B46 tube,AISI 50B46 mould,AISI 50B46 round ingot,AISI 50B46 cold-rolled steel,AISI 50B46 coil,AISI 50B46 strap steel,AISI 50B46 hot-rolled steel,AISI 50B46 medium plate, AISI 50B46 heavy plate,AISI 50B46 shapped bar,AISI 50B46 hexahedral bar,AISI 50B46,AISI 50B46 slab ingot,AISI 50B46 slab,AISI 50B46 price,AISI 50B46 square bar,AISI 50B46 square steel,AISI 50B46 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 50B46.

Current Location:Home » Products » Alloy steel » AISI 50B46

Product category

AISI 50B46

Data Table for:Products: Alloy steel:AISI 50B46

AISI 50B46 properties and heat treatment forged piece, Including AISI 50B46 application and specifications, We have all specifications,Including AISI 50B46 steel plate, AISI 50B46 sheet, AISI 50B46 square steel, AISI 50B46 flat bar,AISI 50B46 round bar,AISI 50B46 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 50B46 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 50B46 and Standards

Designations
United States: ASTM A322 , ASTM A519 , SAE J404 , SAE J412 , SAE J770 , UNS G50461

Chemical Composition
Element
Weight %
C
 0.44-0.49 
Mn
 0.75-1.00 
P
 0.035 (max) 
S
 0.04 (max) 
Si
 0.15-0.30 
Cr
 0.20-0.35 
B
 0.0005-0.003 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Tensile Strength (Mpa)
1779 
25 
oil quenched, fine grained, tempered at 315°C
Yield Strength (Mpa)
1620 
Elongation (%)
10 
Reduction in Area (%)
37 
Hardness (HB)
560 
25 
oil quenched, fine grained, tempered at 205°C



Machining performance

Download AISI 50B46 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:AISI 50B46 steel plate, AISI 50B46 sheet, AISI 50B46 square steel, AISI 50B46 flat bar,AISI 50B46 round bar,AISI 50B46 forgings