Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 4053 plate,AISI 4053 Round Bar,AISI 4053 forgings,AISI 4053 suppliers, AISI 4053 Stock,AISI 4053 sheet, AISI 4053 flat bar, AISI 4053 pipe,AISI 4053 tube,AISI 4053 mould,AISI 4053 round ingot,AISI 4053 cold-rolled steel,AISI 4053 coil,AISI 4053 strap steel,AISI 4053 hot-rolled steel,AISI 4053 medium plate, AISI 4053 heavy plate,AISI 4053 shapped bar,AISI 4053 hexahedral bar,AISI 4053,AISI 4053 slab ingot,AISI 4053 slab,AISI 4053 price,AISI 4053 square bar,AISI 4053 square steel,AISI 4053 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 4053.

Current Location:Home » Products » Alloy steel » AISI 4053

Product category

AISI 4053

Data Table for:Products: Alloy steel:AISI 4053

AISI 4053 properties and heat treatment forged piece, Including AISI 4053 application and specifications, We have all specifications,Including AISI 4053 steel plate, AISI 4053 sheet, AISI 4053 square steel, AISI 4053 flat bar,AISI 4053 round bar,AISI 4053 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 4053 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 4053 and Standards

AISI 4053 steel (UNS G40530)
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel

Key Words: UNS G40530

Physical Properties Metric English Comments
Density  7.75 g/cc 0.280 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  495 495
Tensile Strength, Ultimate  1724 MPa 250000 psi
Tensile Strength, Yield  1538 MPa
@Strain 0.200 %
223100 psi
@Strain 0.200 %
Elongation at Break  12.0 % 12.0 %
Modulus of Elasticity  201 - 209 GPa 29200 - 30300 ksi
Bulk Modulus  160 - 170 GPa 23200 - 24700 ksi
Poissons Ratio  0.270 - 0.300 0.270 - 0.300
Shear Modulus  81.0 - 82.0 GPa 11700 - 11900 ksi




Machining performance

Download AISI 4053 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.