Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 301 plate,AISI 301 Round Bar,AISI 301 forgings,AISI 301 suppliers, AISI 301 Stock,AISI 301 sheet, AISI 301 flat bar, AISI 301 pipe,AISI 301 tube,AISI 301 mould,AISI 301 round ingot,AISI 301 cold-rolled steel,AISI 301 coil,AISI 301 strap steel,AISI 301 hot-rolled steel,AISI 301 medium plate, AISI 301 heavy plate,AISI 301 shapped bar,AISI 301 hexahedral bar,AISI 301,AISI 301 slab ingot,AISI 301 slab,AISI 301 price,AISI 301 square bar,AISI 301 square steel,AISI 301 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 301.

Current Location:Home » Products » Stainless Steel » AISI 301

Product category

AISI 301

Data Table for:Products: Stainless Steel:AISI 301

AISI 301 properties and heat treatment forged piece, Including AISI 301 application and specifications, We have all specifications,Including AISI 301 steel plate, AISI 301 sheet, AISI 301 square steel, AISI 301 flat bar,AISI 301 round bar,AISI 301 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 301 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 301 and Standards

Chemical Composition
Element Weight %
C  0.15 
Mn  2.00 
Si  1.00 
Cr  16.0-18.0 
Ni  6.0-8.0 
P  0.045 
S  0.03 
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 8 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 193 25  
Tensile Strength (Mpa) 515  25     annealed (sheet, strip) 
Yield Strength (Mpa) 205 
Elongation (%) 40 
Reduction in Area (%)  
Hardness (HRB) 88 (max)  25  annealed (bar, wire, plate, sheet, strip) 
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 8 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 193 25  
Tensile Strength (Mpa) 515  25  annealed (sheet, strip)
Yield Strength (Mpa) 205 
Elongation (%) 40 
Reduction in Area (%)  
Hardness (HRB) 88 (max)  25  annealed (bar, wire, plate, sheet, strip) 
Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 17  0-100 more  
Thermal Conductivity (W/m-K) 16.2  100 more  
Specific Heat (J/kg-K) 500  0-100   
Electric Properties
Properties  Conditions 
T (°C) Treatment
Electric Resistivity (10-9W-m) 720  25   



Machining performance

Download AISI 301 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.