Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelAISI 12L14 plate,AISI 12L14 Round Bar,AISI 12L14 forgings,AISI 12L14 suppliers, AISI 12L14 Stock,AISI 12L14 sheet, AISI 12L14 flat bar, AISI 12L14 pipe,AISI 12L14 tube,AISI 12L14 mould,AISI 12L14 round ingot,AISI 12L14 cold-rolled steel,AISI 12L14 coil,AISI 12L14 strap steel,AISI 12L14 hot-rolled steel,AISI 12L14 medium plate, AISI 12L14 heavy plate,AISI 12L14 shapped bar,AISI 12L14 hexahedral bar,AISI 12L14,AISI 12L14 slab ingot,AISI 12L14 slab,AISI 12L14 price,AISI 12L14 square bar,AISI 12L14 square steel,AISI 12L14 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 12L14.

Current Location:Home » Products » Carbon steel » AISI 12L14

Product category

AISI 12L14

Data Table for:Products: Carbon steel:AISI 12L14

AISI 12L14 properties and heat treatment forged piece, Including AISI 12L14 application and specifications, We have all specifications,Including AISI 12L14 steel plate, AISI 12L14 sheet, AISI 12L14 square steel, AISI 12L14 flat bar,AISI 12L14 round bar,AISI 12L14 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 12L14 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 12L14 and Standards

Category  steel
Class  Carbon steel
Type  Standard resulfurized and rephosphorized
Common Names  Lead steel
Designations  Germany: DIN 1.0718
Italy: UNI 9 SMnPb 23
Japan: JIS SUM 22 L , JIS SUM 24 L
Sweden: SS 1914
United States: ASTM A108 , ASTM A29 , SAE J403 , SAE J412 , SAE J414 , UNS G12144

Composition
Element Weight %
C  0.15 (max) 
Mn  0.85-1.15 
P  0.04-0.09 
S  0.26-0.35 
Pb  0.15-0.35 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 540  25  cold drawn (round bar (19-38 mm)) more
Yield Strength (Mpa) 415 
Elongation (%) 10 
Reduction in Area (%) 35 
Hardness (HB) 163  25  cold drawn (round bar (19-38 mm)) more




Machining performance

Download AISI 12L14 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.