Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelSAE 950D HSLA Steel plate,SAE 950D HSLA Steel Round Bar,SAE 950D HSLA Steel forgings,SAE 950D HSLA Steel suppliers, SAE 950D HSLA Steel Stock,SAE 950D HSLA Steel sheet, SAE 950D HSLA Steel flat bar, SAE 950D HSLA Steel pipe,SAE 950D HSLA Steel tube,SAE 950D HSLA Steel mould,SAE 950D HSLA Steel round ingot,SAE 950D HSLA Steel cold-rolled steel,SAE 950D HSLA Steel coil,SAE 950D HSLA Steel strap steel,SAE 950D HSLA Steel hot-rolled steel,SAE 950D HSLA Steel medium plate, SAE 950D HSLA Steel heavy plate,SAE 950D HSLA Steel shapped bar,SAE 950D HSLA Steel hexahedral bar,SAE 950D HSLA Steel,SAE 950D HSLA Steel slab ingot,SAE 950D HSLA Steel slab,SAE 950D HSLA Steel price,SAE 950D HSLA Steel square bar,SAE 950D HSLA Steel square steel,SAE 950D HSLA Steel wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SAE 950D HSLA Steel.

Current Location:Home » Products » Stainless Steel » SAE 950D HSLA Steel

Product category

SAE 950D HSLA Steel

Data Table for:Products: Stainless Steel:SAE 950D HSLA Steel

SAE 950D HSLA Steel properties and heat treatment forged piece, Including SAE 950D HSLA Steel application and specifications, We have all specifications,Including SAE 950D HSLA Steel steel plate, SAE 950D HSLA Steel sheet, SAE 950D HSLA Steel square steel, SAE 950D HSLA Steel flat bar,SAE 950D HSLA Steel round bar,SAE 950D HSLA Steel forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SAE 950D HSLA Steel has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SAE 950D HSLA Steel and Standards

Product Description:

High-Strength Low-Alloy Steel

SAE 950D HSLA steel

Chemical Composition

Element
Weight %
C
 0.15 
Mn
 1.00 
P
 0.15 
S
 0.05 
Si
 0.90 

Mechanical Properties

Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Tensile Strength (Mpa)
460 
25 
(sheet and strip, plate, shapes and bar to 38-76 mm)
Yield Strength (Mpa)
310 
Elongation (%)
24 
Reduction in Area (%)
 




Machining performance

Download SAE 950D HSLA Steel the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:SAE 950D HSLA Steel steel plate, SAE 950D HSLA Steel sheet, SAE 950D HSLA Steel square steel, SAE 950D HSLA Steel flat bar,SAE 950D HSLA Steel round bar,SAE 950D HSLA Steel forgings