Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel75Ni8 plate,75Ni8 Round Bar,75Ni8 forgings,75Ni8 suppliers, 75Ni8 Stock,75Ni8 sheet, 75Ni8 flat bar, 75Ni8 pipe,75Ni8 tube,75Ni8 mould,75Ni8 round ingot,75Ni8 cold-rolled steel,75Ni8 coil,75Ni8 strap steel,75Ni8 hot-rolled steel,75Ni8 medium plate, 75Ni8 heavy plate,75Ni8 shapped bar,75Ni8 hexahedral bar,75Ni8,75Ni8 slab ingot,75Ni8 slab,75Ni8 price,75Ni8 square bar,75Ni8 square steel,75Ni8 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 75Ni8.

Current Location:Home » Products » Alloy steel » 75Ni8

Product category

75Ni8

Data Table for:Products: Alloy steel:75Ni8

75Ni8 properties and heat treatment forged piece, Including 75Ni8 application and specifications, We have all specifications,Including 75Ni8 steel plate, 75Ni8 sheet, 75Ni8 square steel, 75Ni8 flat bar,75Ni8 round bar,75Ni8 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 75Ni8 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 75Ni8 and Standards

75Ni8   ( 1.5634 )

  Grade :     75Ni8
    Number:     1.5634
    Standard: EN 10132 - 4 : 2000   Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Spring steels and other applications
    Classification:     Cold rolled narrow steel strip for heat treatment. Spring steels and other applications

Chemical composition % of the ladle analysis   of grade   75Ni8 (1.5634)

C Si Mn Ni P S Cr Mo
0.72 - 0.78 0.15 - 0.35 0.3 - 0.5 1.8 - 2.1 max   0.025 max   0.025 max   0.15 max   0.1




Machining performance

Download 75Ni8 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.