Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel50CrMo4 plate,50CrMo4 Round Bar,50CrMo4 forgings,50CrMo4 suppliers, 50CrMo4 Stock,50CrMo4 sheet, 50CrMo4 flat bar, 50CrMo4 pipe,50CrMo4 tube,50CrMo4 mould,50CrMo4 round ingot,50CrMo4 cold-rolled steel,50CrMo4 coil,50CrMo4 strap steel,50CrMo4 hot-rolled steel,50CrMo4 medium plate, 50CrMo4 heavy plate,50CrMo4 shapped bar,50CrMo4 hexahedral bar,50CrMo4,50CrMo4 slab ingot,50CrMo4 slab,50CrMo4 price,50CrMo4 square bar,50CrMo4 square steel,50CrMo4 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 50CrMo4.

Current Location:Home » Products » Alloy steel » 50CrMo4

Product category

50CrMo4

Data Table for:Products: Alloy steel:50CrMo4

50CrMo4 properties and heat treatment forged piece, Including 50CrMo4 application and specifications, We have all specifications,Including 50CrMo4 steel plate, 50CrMo4 sheet, 50CrMo4 square steel, 50CrMo4 flat bar,50CrMo4 round bar,50CrMo4 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 50CrMo4 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 50CrMo4 and Standards

50CrMo4   ( 1.7228 )

 

Chemical composition % of the ladle analysis   of grade   50CrMo4 (1.7228)

    Grade :     50CrMo4     Number:     1.7228     Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steel without boron

Equivalent grades of grade   50CrMo4 (1.7228)
Germany
DIN,WNr
England
BS
China
GB
International
ISO
50CrMo4
708M50
50CrMo
50CrMo4

C Si Mn P S Cr Mo 0.46 - 0.54 max   0.4 0.5 - 0.8 max   0.025 max   0.035 0.9 - 1.2 0.15 - 0.3




Machining performance

Download 50CrMo4 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:50CrMo4 steel plate, 50CrMo4 sheet, 50CrMo4 square steel, 50CrMo4 flat bar,50CrMo4 round bar,50CrMo4 forgings