Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless Steel4Cr5MoSiV plate,4Cr5MoSiV Round Bar,4Cr5MoSiV forgings,4Cr5MoSiV suppliers, 4Cr5MoSiV Stock,4Cr5MoSiV sheet, 4Cr5MoSiV flat bar, 4Cr5MoSiV pipe,4Cr5MoSiV tube,4Cr5MoSiV mould,4Cr5MoSiV round ingot,4Cr5MoSiV cold-rolled steel,4Cr5MoSiV coil,4Cr5MoSiV strap steel,4Cr5MoSiV hot-rolled steel,4Cr5MoSiV medium plate, 4Cr5MoSiV heavy plate,4Cr5MoSiV shapped bar,4Cr5MoSiV hexahedral bar,4Cr5MoSiV,4Cr5MoSiV slab ingot,4Cr5MoSiV slab,4Cr5MoSiV price,4Cr5MoSiV square bar,4Cr5MoSiV square steel,4Cr5MoSiV wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 4Cr5MoSiV.

Current Location:Home » Products » Stainless Steel » 4Cr5MoSiV

Product category

4Cr5MoSiV

Data Table for:Products: Stainless Steel:4Cr5MoSiV

4Cr5MoSiV properties and heat treatment forged piece, Including 4Cr5MoSiV application and specifications, We have all specifications,Including 4Cr5MoSiV steel plate, 4Cr5MoSiV sheet, 4Cr5MoSiV square steel, 4Cr5MoSiV flat bar,4Cr5MoSiV round bar,4Cr5MoSiV forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 4Cr5MoSiV has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 4Cr5MoSiV and Standards

Step Shaft 4Cr5MoSiV Tube 4Cr5MoSiV Pie-shaped 4Cr5MoSiV Ring 4Cr5MoSiV Module 4Cr5MoSiV Large valves of the main 4Cr5MoSiV Other Profiled Forgings 4Cr5MoSiV

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download 4Cr5MoSiV the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:4Cr5MoSiV steel plate, 4Cr5MoSiV sheet, 4Cr5MoSiV square steel, 4Cr5MoSiV flat bar,4Cr5MoSiV round bar,4Cr5MoSiV forgings