Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel434 plate,434 Round Bar,434 forgings,434 suppliers, 434 Stock,434 sheet, 434 flat bar, 434 pipe,434 tube,434 mould,434 round ingot,434 cold-rolled steel,434 coil,434 strap steel,434 hot-rolled steel,434 medium plate, 434 heavy plate,434 shapped bar,434 hexahedral bar,434,434 slab ingot,434 slab,434 price,434 square bar,434 square steel,434 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 434.

Current Location:Home » Products » Alloy steel » 434

Product category

434

Data Table for:Products: Alloy steel:434

434 properties and heat treatment forged piece, Including 434 application and specifications, We have all specifications,Including 434 steel plate, 434 sheet, 434 square steel, 434 flat bar,434 round bar,434 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 434 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 434 and Standards

Alloy: T 434 Stainless

 

Nominal Composition in Percent:

 

            Cr                    17.00

            Mo                   1.00

            Fe                  Balance

            Si                    1.00

            Mn                   2.00

            C                     0.120

            P                     0.040

            S                     0.030

 

 

UNS Number: S43400

 

Other Standard Specifications: ------- 

 

Density: -- g/cm3 (-- lbs/in2)

 

Exceptional Properties: -------




Machining performance

Download 434 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:434 steel plate, 434 sheet, 434 square steel, 434 flat bar,434 round bar,434 forgings