Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel41CrS4 plate,41CrS4 Round Bar,41CrS4 forgings,41CrS4 suppliers, 41CrS4 Stock,41CrS4 sheet, 41CrS4 flat bar, 41CrS4 pipe,41CrS4 tube,41CrS4 mould,41CrS4 round ingot,41CrS4 cold-rolled steel,41CrS4 coil,41CrS4 strap steel,41CrS4 hot-rolled steel,41CrS4 medium plate, 41CrS4 heavy plate,41CrS4 shapped bar,41CrS4 hexahedral bar,41CrS4,41CrS4 slab ingot,41CrS4 slab,41CrS4 price,41CrS4 square bar,41CrS4 square steel,41CrS4 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 41CrS4.

Current Location:Home » Products » Alloy steel » 41CrS4

Product category

41CrS4

Data Table for:Products: Alloy steel:41CrS4

41CrS4 properties and heat treatment forged piece, Including 41CrS4 application and specifications, We have all specifications,Including 41CrS4 steel plate, 41CrS4 sheet, 41CrS4 square steel, 41CrS4 flat bar,41CrS4 round bar,41CrS4 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 41CrS4 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 41CrS4 and Standards

41CrS4   ( 1.7039 )

 

Chemical composition % of the ladle analysis   of grade   41CrS4 (1.7039)

    Grade :     41CrS4     Number:     1.7039     Standard: EN 10277 - 5 : 2008   Bright steel products. Technical delivery conditions. steels for quenching and tempering
EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steels for quenching and tempering

C Si Mn P S Cr 0.38 - 0.45 max   0.4 0.6 - 0.9 max   0.025 0.02 - 0.04 0.9 - 1.2

Equivalent grades of grade   41CrS4 (1.7039)

Germany
DIN,WNr
France
AFNOR
Italy
UNI
Spain
UNE
Sweden
SS
Russia
GOST
International
ISO
41CrS4
42C4u
41Cr4
42Cr41
2245
40KH
41CrS4



Machining performance

Download 41CrS4 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.