Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel39NiCrMo3 plate,39NiCrMo3 Round Bar,39NiCrMo3 forgings,39NiCrMo3 suppliers, 39NiCrMo3 Stock,39NiCrMo3 sheet, 39NiCrMo3 flat bar, 39NiCrMo3 pipe,39NiCrMo3 tube,39NiCrMo3 mould,39NiCrMo3 round ingot,39NiCrMo3 cold-rolled steel,39NiCrMo3 coil,39NiCrMo3 strap steel,39NiCrMo3 hot-rolled steel,39NiCrMo3 medium plate, 39NiCrMo3 heavy plate,39NiCrMo3 shapped bar,39NiCrMo3 hexahedral bar,39NiCrMo3,39NiCrMo3 slab ingot,39NiCrMo3 slab,39NiCrMo3 price,39NiCrMo3 square bar,39NiCrMo3 square steel,39NiCrMo3 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 39NiCrMo3.

Current Location:Home » Products » Alloy steel » 39NiCrMo3

Product category

39NiCrMo3

Data Table for:Products: Alloy steel:39NiCrMo3

39NiCrMo3 properties and heat treatment forged piece, Including 39NiCrMo3 application and specifications, We have all specifications,Including 39NiCrMo3 steel plate, 39NiCrMo3 sheet, 39NiCrMo3 square steel, 39NiCrMo3 flat bar,39NiCrMo3 round bar,39NiCrMo3 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 39NiCrMo3 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 39NiCrMo3 and Standards

39NiCrMo3   ( 1.6510 )

 

Chemical composition % of the ladle analysis   of grade   39NiCrMo3 (1.6510)

    Grade :     39NiCrMo3     Number:     1.6510     Standard: EN 10277 - 5 : 2008   Bright steel products. Technical delivery conditions. steels for quenching and tempering
EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steels for quenching and tempering

Equivalent grades of grade   39NiCrMo3 (1.6510)
Italy
UNI
39NiCrMo3

C Si Mn Ni P S Cr Mo 0.35 - 0.43 max   0.4 0.5 - 0.8 0.7 - 1 max   0.025 max   0.035 0.6 - 1 0.15 - 0.25




Machining performance

Download 39NiCrMo3 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.