Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel38MnB5 plate,38MnB5 Round Bar,38MnB5 forgings,38MnB5 suppliers, 38MnB5 Stock,38MnB5 sheet, 38MnB5 flat bar, 38MnB5 pipe,38MnB5 tube,38MnB5 mould,38MnB5 round ingot,38MnB5 cold-rolled steel,38MnB5 coil,38MnB5 strap steel,38MnB5 hot-rolled steel,38MnB5 medium plate, 38MnB5 heavy plate,38MnB5 shapped bar,38MnB5 hexahedral bar,38MnB5,38MnB5 slab ingot,38MnB5 slab,38MnB5 price,38MnB5 square bar,38MnB5 square steel,38MnB5 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 38MnB5.

Current Location:Home » Products » Alloy steel » 38MnB5

Product category

38MnB5

Data Table for:Products: Alloy steel:38MnB5

38MnB5 properties and heat treatment forged piece, Including 38MnB5 application and specifications, We have all specifications,Including 38MnB5 steel plate, 38MnB5 sheet, 38MnB5 square steel, 38MnB5 flat bar,38MnB5 round bar,38MnB5 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 38MnB5 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 38MnB5 and Standards

38MnB5   ( 1.5532 )

 

Chemical composition % of the ladle analysis   of grade   38MnB5 (1.5532)

    Grade :     38MnB5     Number:     1.5532     Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steel with boron

C Si Mn P S B 0.36 - 0.42 max   0.4 1.15 - 1.45 max   0.025 max   0.035 0.0008 - 0.005




Machining performance

Download 38MnB5 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:38MnB5 steel plate, 38MnB5 sheet, 38MnB5 square steel, 38MnB5 flat bar,38MnB5 round bar,38MnB5 forgings