Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel38Cr2 plate,38Cr2 Round Bar,38Cr2 forgings,38Cr2 suppliers, 38Cr2 Stock,38Cr2 sheet, 38Cr2 flat bar, 38Cr2 pipe,38Cr2 tube,38Cr2 mould,38Cr2 round ingot,38Cr2 cold-rolled steel,38Cr2 coil,38Cr2 strap steel,38Cr2 hot-rolled steel,38Cr2 medium plate, 38Cr2 heavy plate,38Cr2 shapped bar,38Cr2 hexahedral bar,38Cr2,38Cr2 slab ingot,38Cr2 slab,38Cr2 price,38Cr2 square bar,38Cr2 square steel,38Cr2 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 38Cr2.

Current Location:Home » Products » Alloy steel » 38Cr2

Product category

38Cr2

Data Table for:Products: Alloy steel:38Cr2

38Cr2 properties and heat treatment forged piece, Including 38Cr2 application and specifications, We have all specifications,Including 38Cr2 steel plate, 38Cr2 sheet, 38Cr2 square steel, 38Cr2 flat bar,38Cr2 round bar,38Cr2 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 38Cr2 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 38Cr2 and Standards

38Cr2   ( 1.7003 )

 

Chemical composition % of the ladle analysis   of grade   38Cr2 (1.7003)

    Grade :     38Cr2     Number:     1.7003     Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steel without boron

Equivalent grades of grade   38Cr2 (1.7003)
Germany
DIN,WNr
France
AFNOR
38Cr2
38C2

C Si Mn P S Cr 0.35 - 0.42 max   0.4 0.5 - 0.8 max   0.025 max   0.035 0.4 - 0.6




Machining performance

Download 38Cr2 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:38Cr2 steel plate, 38Cr2 sheet, 38Cr2 square steel, 38Cr2 flat bar,38Cr2 round bar,38Cr2 forgings