Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel35NiCr6 plate,35NiCr6 Round Bar,35NiCr6 forgings,35NiCr6 suppliers, 35NiCr6 Stock,35NiCr6 sheet, 35NiCr6 flat bar, 35NiCr6 pipe,35NiCr6 tube,35NiCr6 mould,35NiCr6 round ingot,35NiCr6 cold-rolled steel,35NiCr6 coil,35NiCr6 strap steel,35NiCr6 hot-rolled steel,35NiCr6 medium plate, 35NiCr6 heavy plate,35NiCr6 shapped bar,35NiCr6 hexahedral bar,35NiCr6,35NiCr6 slab ingot,35NiCr6 slab,35NiCr6 price,35NiCr6 square bar,35NiCr6 square steel,35NiCr6 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 35NiCr6.

Current Location:Home » Products » Alloy steel » 35NiCr6

Product category

35NiCr6

Data Table for:Products: Alloy steel:35NiCr6

35NiCr6 properties and heat treatment forged piece, Including 35NiCr6 application and specifications, We have all specifications,Including 35NiCr6 steel plate, 35NiCr6 sheet, 35NiCr6 square steel, 35NiCr6 flat bar,35NiCr6 round bar,35NiCr6 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 35NiCr6 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 35NiCr6 and Standards

35NiCr6 ( 1.5815 )

Grade :     35NiCr6
    Number:     1.5815
    Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels
    Classification:     steel without boron

Chemical composition % of the ladle analysis   of grade   35NiCr6 (1.5815)

C Si Mn Ni P S Cr
0.3 - 0.37 max   0.4 0.6 - 0.9 1.2 - 1.6 max   0.025 max   0.025 0.9 - 1.1

Equivalent grades of grade   35NiCr6 (1.5815)

Germany
DIN,WNr
35NiCr6




Machining performance

Download 35NiCr6 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.