Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.7037 plate,1.7037 Round Bar,1.7037 forgings,1.7037 suppliers, 1.7037 Stock,1.7037 sheet, 1.7037 flat bar, 1.7037 pipe,1.7037 tube,1.7037 mould,1.7037 round ingot,1.7037 cold-rolled steel,1.7037 coil,1.7037 strap steel,1.7037 hot-rolled steel,1.7037 medium plate, 1.7037 heavy plate,1.7037 shapped bar,1.7037 hexahedral bar,1.7037,1.7037 slab ingot,1.7037 slab,1.7037 price,1.7037 square bar,1.7037 square steel,1.7037 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.7037.

Current Location:Home » Products » Alloy steel » 1.7037

Product category

1.7037

Data Table for:Products: Alloy steel:1.7037

1.7037 properties and heat treatment forged piece, Including 1.7037 application and specifications, We have all specifications,Including 1.7037 steel plate, 1.7037 sheet, 1.7037 square steel, 1.7037 flat bar,1.7037 round bar,1.7037 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.7037 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.7037 and Standards

34CrS4   ( 1.7037 )  
 
Chemical composition % of the ladle analysis   of grade   34CrS4 (1.7037)

    Grade :     34CrS4     Number:     1.7037     Standard: EN 10277 - 5 : 2008   Bright steel products. Technical delivery conditions. steels for quenching and tempering
EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels     Classification:     steels for quenching and tempering

Equivalent grades of grade   34CrS4 (1.7037)
Germany
DIN,WNr
France
AFNOR
International
ISO
34CrS4
32C4u
34CrS4

C Si Mn P S Cr 0.3 - 0.7 max   0.4 0.6 - 0.9 max   0.025 0.02 - 0.04 0.9 - 1.2




Machining performance

Download 1.7037 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.