Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.6580 plate,1.6580 Round Bar,1.6580 forgings,1.6580 suppliers, 1.6580 Stock,1.6580 sheet, 1.6580 flat bar, 1.6580 pipe,1.6580 tube,1.6580 mould,1.6580 round ingot,1.6580 cold-rolled steel,1.6580 coil,1.6580 strap steel,1.6580 hot-rolled steel,1.6580 medium plate, 1.6580 heavy plate,1.6580 shapped bar,1.6580 hexahedral bar,1.6580,1.6580 slab ingot,1.6580 slab,1.6580 price,1.6580 square bar,1.6580 square steel,1.6580 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.6580.

Current Location:Home » Products » Alloy steel » 1.6580

Product category

1.6580

Data Table for:Products: Alloy steel:1.6580

1.6580 properties and heat treatment forged piece, Including 1.6580 application and specifications, We have all specifications,Including 1.6580 steel plate, 1.6580 sheet, 1.6580 square steel, 1.6580 flat bar,1.6580 round bar,1.6580 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.6580 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.6580 and Standards

30CrNiMo8 ( 1.6580 )

 

Grade :     30CrNiMo8
    Number:     1.6580
    Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels
    Classification:     steel without boron

 

Chemical composition % of the ladle analysis of grade 30CrNiMo8 (1.6580)

 

C Si Mn Ni P S Cr Mo
0.26 - 0.34 max   0.4 0.5 - 0.8 1.8 - 2.2 max   0.025 max   0.035 1.8 - 2.2 0.3 - 0.5

 

Equivalent grades of grade   30CrNiMo8 (1.6580)

 

Germany
DIN,WNr
France
AFNOR
England
BS
China
GB
Russia
GOST
International
ISO
30CrNiMo8
30CND8
823M30
30Cr2Ni2Mo
3KH3M3F
31CrNiMo8

 




Machining performance

Download 1.6580 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:1.6580 steel plate, 1.6580 sheet, 1.6580 square steel, 1.6580 flat bar,1.6580 round bar,1.6580 forgings