DIN X23CrNi17 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » X23CrNi17
28NiMo17
1.2747
35NiCrMo16
1.2766
X6NiCrTi26-15
1.2779
X16CrNiSi25-20
1.2782
X13NiCrSi36-16
1.2786 - DIN
- Germany
- Hot working alloy tool steel
Chemical composition % of the ladle analysis of grade X23CrNi17
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) |
| 0.10-0.25 | Max 1.00 | Max 1.00 | Max 0.035 | Max 0.035 | 15.5-18.0 | 1.00-2.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 598 (≥) | 775 (≥) | 13 | 33 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 663 (≥) | 622 (≥) | 22 | 42 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 141 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 218 | 565 | 499 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |