Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyZ10CNS25-20 plate,Z10CNS25-20 Round Bar,Z10CNS25-20 forgings,Z10CNS25-20 suppliers, Z10CNS25-20 Stock,Z10CNS25-20 sheet, Z10CNS25-20 flat bar, Z10CNS25-20 pipe,Z10CNS25-20 tube,Z10CNS25-20 mould,Z10CNS25-20 round ingot,Z10CNS25-20 cold-rolled steel,Z10CNS25-20 coil,Z10CNS25-20 strap steel,Z10CNS25-20 hot-rolled steel,Z10CNS25-20 medium plate, Z10CNS25-20 heavy plate,Z10CNS25-20 shapped bar,Z10CNS25-20 hexahedral bar,Z10CNS25-20,Z10CNS25-20 slab ingot,Z10CNS25-20 slab,Z10CNS25-20 price,Z10CNS25-20 square bar,Z10CNS25-20 square steel,Z10CNS25-20 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Z10CNS25-20.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Z10CNS25-20

Product category

Z10CNS25-20

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Z10CNS25-20

Z10CNS25-20 properties and heat treatment forged piece, Including Z10CNS25-20 application and specifications, We have all specifications,Including Z10CNS25-20 steel plate, Z10CNS25-20 sheet, Z10CNS25-20 square steel, Z10CNS25-20 flat bar,Z10CNS25-20 round bar,Z10CNS25-20 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Z10CNS25-20 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Z10CNS25-20 and Standards

Grade :   08KH20N14S2   ( 08Х20Н14С2 ) (   0Х20Н14С2     ЭИ732   )
      Classification :   High alloy high-temperature steel
      Equivalent steels:  

Chemical composition in % for grade   08KH20N14S2   ( 08Х20Н14С2 ) GOST   5632 - 72
C Si Mn Ni S P Cr
max   0.08 2 - 3 max   1.5 12 - 15 max   0.025 max   0.035 19 - 22
Mechanical properties under Т=20oС for grade   08KH20N14S2   ( 08Х20Н14С2 )

 

Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
      550 250 40 50 1000 Guenching 1000 - 1150oC, air,
Pipe cooling strain, GOST 9941-81     510   35      
Pipe hot strain, GOST 9940-81     510   35      
Physical properties for grade   08KH20N14S2   ( 08Х20Н14С2 )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20       7700    

Equivalent steels for grade   08KH20N14S2   ( 08Х20Н14С2 )

 

Warning! Indicated both exact and nearest equivalents.

 

USA Germany Japan France England European Spain China
- DIN,WNr JIS AFNOR BS EN UNE GB
XM-15
X15CrNiSi20-12
SUH309
Z10CNS25-20
Z17CNS20-12
X15CrNiSi20-12
X15CrNiSi20-12
X15CrNiSi20-12
1Cr20Ni14Si2



Machining performance

Download Z10CNS25-20 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.