Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelX70CrMo15 plate,X70CrMo15 Round Bar,X70CrMo15 forgings,X70CrMo15 suppliers, X70CrMo15 Stock,X70CrMo15 sheet, X70CrMo15 flat bar, X70CrMo15 pipe,X70CrMo15 tube,X70CrMo15 mould,X70CrMo15 round ingot,X70CrMo15 cold-rolled steel,X70CrMo15 coil,X70CrMo15 strap steel,X70CrMo15 hot-rolled steel,X70CrMo15 medium plate, X70CrMo15 heavy plate,X70CrMo15 shapped bar,X70CrMo15 hexahedral bar,X70CrMo15,X70CrMo15 slab ingot,X70CrMo15 slab,X70CrMo15 price,X70CrMo15 square bar,X70CrMo15 square steel,X70CrMo15 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of X70CrMo15.

Current Location:Home » Products » Stainless Steel » X70CrMo15

Product category

X70CrMo15

Data Table for:Products: Stainless Steel:X70CrMo15

X70CrMo15 properties and heat treatment forged piece, Including X70CrMo15 application and specifications, We have all specifications,Including X70CrMo15 steel plate, X70CrMo15 sheet, X70CrMo15 square steel, X70CrMo15 flat bar,X70CrMo15 round bar,X70CrMo15 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the X70CrMo15 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade X70CrMo15 and Standards

X70CrMo15 ( 1.4109 )

Grade :     X70CrMo15
    Number:     1.4109
    Standard: EN 10088 - 3 : 2005   stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
    Classification:     Martensitic stainless steels-special grades
    Equivalent grades:     No information

Chemical composition % of the ladle analysis   of grade   X70CrMo15 (1.4109)
C Si Mn P S Cr Mo
0.6 - 0.75 max   0.7 max   1 max   0.04 max   0.03 14 - 16 0.4 - 0.8
Mechanical properties
Mechanische Eigenschaften
Caracteristiques mecaniques

ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d’elasticite minimale
Rm Tensile strength / Zugfestigkeit / Resistance a la traction
A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal
J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc




Machining performance

Download X70CrMo15 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.