Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelUNS T30103 plate,UNS T30103 Round Bar,UNS T30103 forgings,UNS T30103 suppliers, UNS T30103 Stock,UNS T30103 sheet, UNS T30103 flat bar, UNS T30103 pipe,UNS T30103 tube,UNS T30103 mould,UNS T30103 round ingot,UNS T30103 cold-rolled steel,UNS T30103 coil,UNS T30103 strap steel,UNS T30103 hot-rolled steel,UNS T30103 medium plate, UNS T30103 heavy plate,UNS T30103 shapped bar,UNS T30103 hexahedral bar,UNS T30103,UNS T30103 slab ingot,UNS T30103 slab,UNS T30103 price,UNS T30103 square bar,UNS T30103 square steel,UNS T30103 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS T30103.

Current Location:Home » Products » Tool steel » UNS T30103

Product category

UNS T30103

Data Table for:Products: Tool steel:UNS T30103

UNS T30103 properties and heat treatment forged piece, Including UNS T30103 application and specifications, We have all specifications,Including UNS T30103 steel plate, UNS T30103 sheet, UNS T30103 square steel, UNS T30103 flat bar,UNS T30103 round bar,UNS T30103 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS T30103 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS T30103 and Standards

C
Si
Mn
P
S
Cr Ni
1.2-1.3  0.1-0.5  0.4-0.6 0.03  0.03   4.75-5.5  
Mo Al Cu Nb Ti V Ce
 0.9-1.4         0.8-1.4  




Machining performance

Download UNS T30103 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:UNS T30103 steel plate, UNS T30103 sheet, UNS T30103 square steel, UNS T30103 flat bar,UNS T30103 round bar,UNS T30103 forgings