Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S43903 plate,UNS S43903 Round Bar,UNS S43903 forgings,UNS S43903 suppliers, UNS S43903 Stock,UNS S43903 sheet, UNS S43903 flat bar, UNS S43903 pipe,UNS S43903 tube,UNS S43903 mould,UNS S43903 round ingot,UNS S43903 cold-rolled steel,UNS S43903 coil,UNS S43903 strap steel,UNS S43903 hot-rolled steel,UNS S43903 medium plate, UNS S43903 heavy plate,UNS S43903 shapped bar,UNS S43903 hexahedral bar,UNS S43903,UNS S43903 slab ingot,UNS S43903 slab,UNS S43903 price,UNS S43903 square bar,UNS S43903 square steel,UNS S43903 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S43903.

Current Location:Home » Products » Stainless Steel » UNS S43903

Product category

UNS S43903

Data Table for:Products: Stainless Steel:UNS S43903

UNS S43903 properties and heat treatment forged piece, Including UNS S43903 application and specifications, We have all specifications,Including UNS S43903 steel plate, UNS S43903 sheet, UNS S43903 square steel, UNS S43903 flat bar,UNS S43903 round bar,UNS S43903 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS S43903 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS S43903 and Standards

C(%): ≤0.014
Si(%): ≤1.00
Mn(%): ≤1.00
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 17.0~19.0
Ni(%): ≤0.50
Mo(%): —
0.20+4(C+N)≤Ti≤1.10,Al≤0.15,N≤0.04




Machining performance

Download UNS S43903 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:UNS S43903 steel plate, UNS S43903 sheet, UNS S43903 square steel, UNS S43903 flat bar,UNS S43903 round bar,UNS S43903 forgings