Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S31640 plate,UNS S31640 Round Bar,UNS S31640 forgings,UNS S31640 suppliers, UNS S31640 Stock,UNS S31640 sheet, UNS S31640 flat bar, UNS S31640 pipe,UNS S31640 tube,UNS S31640 mould,UNS S31640 round ingot,UNS S31640 cold-rolled steel,UNS S31640 coil,UNS S31640 strap steel,UNS S31640 hot-rolled steel,UNS S31640 medium plate, UNS S31640 heavy plate,UNS S31640 shapped bar,UNS S31640 hexahedral bar,UNS S31640,UNS S31640 slab ingot,UNS S31640 slab,UNS S31640 price,UNS S31640 square bar,UNS S31640 square steel,UNS S31640 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S31640.

Current Location:Home » Products » Stainless Steel » UNS S31640

Product category

UNS S31640

Data Table for:Products: Stainless Steel:UNS S31640

UNS S31640 properties and heat treatment forged piece, Including UNS S31640 application and specifications, We have all specifications,Including UNS S31640 steel plate, UNS S31640 sheet, UNS S31640 square steel, UNS S31640 flat bar,UNS S31640 round bar,UNS S31640 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS S31640 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS S31640 and Standards

C(%): ≤0.08
Si(%): ≤1.00
Mn(%): ≤2.00
P(%)≤: 0.045
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): 10.0~14.0
Mo(%): 2.00~3.00
10×C≤b≤1.10,N≤0.10




Machining performance

Download UNS S31640 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.