Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S30323 plate,UNS S30323 Round Bar,UNS S30323 forgings,UNS S30323 suppliers, UNS S30323 Stock,UNS S30323 sheet, UNS S30323 flat bar, UNS S30323 pipe,UNS S30323 tube,UNS S30323 mould,UNS S30323 round ingot,UNS S30323 cold-rolled steel,UNS S30323 coil,UNS S30323 strap steel,UNS S30323 hot-rolled steel,UNS S30323 medium plate, UNS S30323 heavy plate,UNS S30323 shapped bar,UNS S30323 hexahedral bar,UNS S30323,UNS S30323 slab ingot,UNS S30323 slab,UNS S30323 price,UNS S30323 square bar,UNS S30323 square steel,UNS S30323 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S30323.

Current Location:Home » Products » Stainless Steel » UNS S30323

Product category

UNS S30323

Data Table for:Products: Stainless Steel:UNS S30323

UNS S30323 properties and heat treatment forged piece, Including UNS S30323 application and specifications, We have all specifications,Including UNS S30323 steel plate, UNS S30323 sheet, UNS S30323 square steel, UNS S30323 flat bar,UNS S30323 round bar,UNS S30323 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS S30323 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS S30323 and Standards

C(%):    ≤0.15
Si(%):    ≤1.00
Mn(%):    ≤2.00
P(%)≤:    0.2
S(%)≤:    0.06
Cr(%):    17.0~19.0
Ni(%):    8.00~10.0
Mo(%):    —
Se≥0.15




Machining performance

Download UNS S30323 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:UNS S30323 steel plate, UNS S30323 sheet, UNS S30323 square steel, UNS S30323 flat bar,UNS S30323 round bar,UNS S30323 forgings