Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelUNS G94151 plate,UNS G94151 Round Bar,UNS G94151 forgings,UNS G94151 suppliers, UNS G94151 Stock,UNS G94151 sheet, UNS G94151 flat bar, UNS G94151 pipe,UNS G94151 tube,UNS G94151 mould,UNS G94151 round ingot,UNS G94151 cold-rolled steel,UNS G94151 coil,UNS G94151 strap steel,UNS G94151 hot-rolled steel,UNS G94151 medium plate, UNS G94151 heavy plate,UNS G94151 shapped bar,UNS G94151 hexahedral bar,UNS G94151,UNS G94151 slab ingot,UNS G94151 slab,UNS G94151 price,UNS G94151 square bar,UNS G94151 square steel,UNS G94151 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS G94151.

Current Location:Home » Products » Alloy steel » UNS G94151

Product category

UNS G94151

Data Table for:Products: Alloy steel:UNS G94151

UNS G94151 properties and heat treatment forged piece, Including UNS G94151 application and specifications, We have all specifications,Including UNS G94151 steel plate, UNS G94151 sheet, UNS G94151 square steel, UNS G94151 flat bar,UNS G94151 round bar,UNS G94151 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS G94151 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS G94151 and Standards

AISI 94B15 steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 9000 Series steel; Low Alloy Steel; Carbon Steel; Low Carbon steel

Key Words: UNS G94151, AMS 6275 A, ASTM A519, SAE J404, SAE J770

Physical Properties Metric English Comments
Density  7.87 g/cc 0.284 lb/in³ field average for steels
 
Mechanical Properties Metric English Comments
Hardness, Brinell  163 - 202 163 - 202 hot rolled and cold drawn
Hardness, Knoop  204 204 Converted from Brinell hardness.
Hardness, Rockwell B  89 89 Converted from Brinell hardness.
Hardness, Vickers  192 192 Converted from Brinell hardness.
Modulus of Elasticity  200 GPa 29000 ksi Estimated
Bulk Modulus  140 GPa 20300 ksi Typical for steel.
Poissons Ratio  0.290 0.290 Calculated
Machinability  70 % 70 % hot rolled and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000174 ohm-cm 0.0000174 ohm-cm Estimated
 
Thermal Properties Metric English Comments
CTE, linear   11.5 µm/m-°C
@Temperature 20.0 °C
6.39 µin/in-°F
@Temperature 68.0 °F
  12.2 µm/m-°C
@Temperature 250 °C
6.78 µin/in-°F
@Temperature 482 °F
Estimated
  13.9 µm/m-°C
@Temperature 500 °C
7.72 µin/in-°F
@Temperature 932 °F
  14.7 µm/m-°C
@Temperature 1000 °C
8.17 µin/in-°F
@Temperature 1830 °F
Specific Heat Capacity  0.472 J/g-°C 0.113 BTU/lb-°F Estimated
Thermal Conductivity  51.9 W/m-K 360 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Boron, B  0.000500 - 0.00300 % 0.000500 - 0.00300 %
Carbon, C  0.130 - 0.180 % 0.130 - 0.180 %
Chromium, Cr  0.300 - 0.500 % 0.300 - 0.500 %
Iron, Fe  97.192 - 98.2895 % 97.192 - 98.2895 % As remainder
Manganese, Mn  0.750 - 1.00 % 0.750 - 1.00 %
Molybdenum, Mo  0.0800 - 0.150 % 0.0800 - 0.150 %
Nickel, Ni  0.300 - 0.600 % 0.300 - 0.600 %
Phosphorous, P  <= 0.0350 % <= 0.0350 %
Silicon, Si  0.150 - 0.300 % 0.150 - 0.300 %
Sulfur, S  <= 0.0400 % <= 0.0400 %

Users viewing this material also viewed the following:
AISI 94B17 Steel
AISI E9310 Steel, direct quenched from pot, tempered at 150°C (300°F), 0.99 mm case depth
AISI 9840 Steel, 540°C (1000°F) temper, 25 mm (1 in.) round
AISI 9260 Steel
AISI 94B15H Steel

M941AA / 8707
 




Machining performance

Download UNS G94151 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.