Our to produce better steel-based products are the main used in industrial manufacturing various types Low alloy high-temperature steelUNS G40230 plate,UNS G40230 Round Bar,UNS G40230 forgings,UNS G40230 suppliers, UNS G40230 Stock,UNS G40230 sheet, UNS G40230 flat bar, UNS G40230 pipe,UNS G40230 tube,UNS G40230 mould,UNS G40230 round ingot,UNS G40230 cold-rolled steel,UNS G40230 coil,UNS G40230 strap steel,UNS G40230 hot-rolled steel,UNS G40230 medium plate, UNS G40230 heavy plate,UNS G40230 shapped bar,UNS G40230 hexahedral bar,UNS G40230,UNS G40230 slab ingot,UNS G40230 slab,UNS G40230 price,UNS G40230 square bar,UNS G40230 square steel,UNS G40230 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS G40230.

Current Location:Home » Products » Low alloy high-temperature steel » UNS G40230

Product category

UNS G40230

Data Table for:Products: Low alloy high-temperature steel:UNS G40230

UNS G40230 properties and heat treatment forged piece, Including UNS G40230 application and specifications, We have all specifications,Including UNS G40230 steel plate, UNS G40230 sheet, UNS G40230 square steel, UNS G40230 flat bar,UNS G40230 round bar,UNS G40230 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS G40230 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS G40230 and Standards

AISI 4023 steel, normalized at 925°C (1700°F), machined to 25 mm (1 in.) rounds, pseudocarburized at 925°C (1700°F), box cooled to RT, reheated to 775°C (1430°F) and oil quenched, 150°C (300°F) temper
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel; Carbon Steel; Low Carbon steel

Material Notes: Specimens were machined to 12.8 mm (0.505 in.) rounds and tested; Forging temp.: 1230°C (2250°F). Normalizing temp.: 900 - 955°C. Carburizing temp.: 900 - 925°C. Tempering temp.: 120 - 175°C.

Key Words: UNS G40230, ASTM A29, ASTM A29M, ASTM A322, ASTM A331, ASTM A519, ASTM A534, ASTM A752, SAE 770, SAE J404, SAE J412, SAE J770

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  223 223
Hardness, Knoop  246 246 Converted from Brinell hardness.
Hardness, Rockwell B  96 96 Converted from Brinell hardness.
Hardness, Rockwell C  18.0 18.0 Converted from Brinell hardness. Value below normal HRC range, for comparison purposes only.
Hardness, Vickers  235 235 Converted from Brinell hardness.
Tensile Strength, Ultimate  724 MPa 105000 psi
Tensile Strength, Yield  415 MPa 60200 psi
Elongation at Break  19.0 % 19.0 % in 50 mm
Reduction of Area  48.0 % 48.0 %
Modulus of Elasticity  205 GPa 29700 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Calculated
Machinability  70 % 70 % hot rolled and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000245 ohm-cm 0.0000245 ohm-cm Typical 4000 series steel
 
Thermal Properties Metric English Comments
Specific Heat Capacity  0.475 J/g-°C 0.114 BTU/lb-°F Typical 4000 series steel
Thermal Conductivity  44.5 W/m-K 309 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.20 - 0.25 % 0.20 - 0.25 %
Iron, Fe  98.13 - 98.75 % 98.13 - 98.75 % As remainder
Manganese, Mn  0.70 - 0.90 % 0.70 - 0.90 %
Molybdenum, Mo  0.20 - 0.30 % 0.20 - 0.30 %
Phosphorous, P  <= 0.035 % <= 0.035 %
Silicon, Si  0.15 - 0.35 % 0.15 - 0.35 %
Sulfur, S  <= 0.040 % <= 0.040 %

Users viewing this material also viewed the following:
AISI 4012 Steel
Overview of materials for AISI 4000 Series Steel
AISI 4024 Steel
AISI 4023 Steel, normalized at 925°C (1700°F), machined to 25 mm (1 in.) rounds, pseudocarburized at 925°C (1700°F), box cooled to RT, reheated to 800°C (1470°F) (1475°F) and oil quenched, 150°C (300°F) temper
AISI 4027 Steel, annealed, 25 mm (1 in.) round

M4023A / 7426
 




Machining performance

Download UNS G40230 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.