Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelSUS440c 440c 9Cr18 plate,SUS440c 440c 9Cr18 Round Bar,SUS440c 440c 9Cr18 forgings,SUS440c 440c 9Cr18 suppliers, SUS440c 440c 9Cr18 Stock,SUS440c 440c 9Cr18 sheet, SUS440c 440c 9Cr18 flat bar, SUS440c 440c 9Cr18 pipe,SUS440c 440c 9Cr18 tube,SUS440c 440c 9Cr18 mould,SUS440c 440c 9Cr18 round ingot,SUS440c 440c 9Cr18 cold-rolled steel,SUS440c 440c 9Cr18 coil,SUS440c 440c 9Cr18 strap steel,SUS440c 440c 9Cr18 hot-rolled steel,SUS440c 440c 9Cr18 medium plate, SUS440c 440c 9Cr18 heavy plate,SUS440c 440c 9Cr18 shapped bar,SUS440c 440c 9Cr18 hexahedral bar,SUS440c 440c 9Cr18,SUS440c 440c 9Cr18 slab ingot,SUS440c 440c 9Cr18 slab,SUS440c 440c 9Cr18 price,SUS440c 440c 9Cr18 square bar,SUS440c 440c 9Cr18 square steel,SUS440c 440c 9Cr18 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SUS440c 440c 9Cr18.

Current Location:Home » Products » Stainless Steel » SUS440c 440c 9Cr18

Product category

SUS440c 440c 9Cr18

Data Table for:Products: Stainless Steel:SUS440c 440c 9Cr18

SUS440c 440c 9Cr18 properties and heat treatment forged piece, Including SUS440c 440c 9Cr18 application and specifications, We have all specifications,Including SUS440c 440c 9Cr18 steel plate, SUS440c 440c 9Cr18 sheet, SUS440c 440c 9Cr18 square steel, SUS440c 440c 9Cr18 flat bar,SUS440c 440c 9Cr18 round bar,SUS440c 440c 9Cr18 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SUS440c 440c 9Cr18 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SUS440c 440c 9Cr18 and Standards

Step Shaft SUS440c Tube SUS440c Pie-shaped 440C Ring 440C Module 440C Large valves of the main 440C Other Profiled Forgings SUS440c

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.
 




Machining performance

Download SUS440c 440c 9Cr18 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:SUS440c 440c 9Cr18 steel plate, SUS440c 440c 9Cr18 sheet, SUS440c 440c 9Cr18 square steel, SUS440c 440c 9Cr18 flat bar,SUS440c 440c 9Cr18 round bar,SUS440c 440c 9Cr18 forgings