SCM435
SCM435 properties and heat treatment forged piece, Including SCM435 application and specifications, We have all specifications，Including SCM435 steel plate, SCM435 sheet, SCM435 square steel, SCM435 flat bar,SCM435 round bar,SCM435 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the SCM435 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade SCM435 and Standards
Execution standard: JIS G4053-2003
Chemical composition
C ：0.33～0.38
Si：0.15～0.35
Mn：0.60～0.90
S ：≤0.030
P ：≤0.030
Cr：0.90～1.20
Ni：≤0.25
Cu：≤0.30
Mo：0.15～0.30
Mechanical properties
Tensile strength σ b (MPa) : frequency 985 (100) the yield strength σ s (MPa) : 835 (85) at the frequency δ 5 (%) : quartile 12 area reduction ψ (%) : quartile 45 impact energy Akv (J) : frequency 63 impact toughness values α kv (J/cm&sup 2;) : frequency 78 (8) hardness: more than 229 HB sample size: sample blank dimensions for 25 mm
characteristics
The static strength, have very high impact toughness and higher fatigue limit, its quench-hardening ability is 40 Cr high, high temperatures high creep strength and sustained intensity, long work temperatures up to 500 ℃; Cold when the deformation plasticity medium, welding sex differences.
use
Used for high load in the important parts, such as vehicle and the engine driving a; The steam turbine generator rotor, spindle, heavy load of the drive shaft, large sections parts.
Machining performance
Download SCM435 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.