Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelS31500 00Cr18Ni5Mo3Si2 3RE60 plate,S31500 00Cr18Ni5Mo3Si2 3RE60 Round Bar,S31500 00Cr18Ni5Mo3Si2 3RE60 forgings,S31500 00Cr18Ni5Mo3Si2 3RE60 suppliers, S31500 00Cr18Ni5Mo3Si2 3RE60 Stock,S31500 00Cr18Ni5Mo3Si2 3RE60 sheet, S31500 00Cr18Ni5Mo3Si2 3RE60 flat bar, S31500 00Cr18Ni5Mo3Si2 3RE60 pipe,S31500 00Cr18Ni5Mo3Si2 3RE60 tube,S31500 00Cr18Ni5Mo3Si2 3RE60 mould,S31500 00Cr18Ni5Mo3Si2 3RE60 round ingot,S31500 00Cr18Ni5Mo3Si2 3RE60 cold-rolled steel,S31500 00Cr18Ni5Mo3Si2 3RE60 coil,S31500 00Cr18Ni5Mo3Si2 3RE60 strap steel,S31500 00Cr18Ni5Mo3Si2 3RE60 hot-rolled steel,S31500 00Cr18Ni5Mo3Si2 3RE60 medium plate, S31500 00Cr18Ni5Mo3Si2 3RE60 heavy plate,S31500 00Cr18Ni5Mo3Si2 3RE60 shapped bar,S31500 00Cr18Ni5Mo3Si2 3RE60 hexahedral bar,S31500 00Cr18Ni5Mo3Si2 3RE60,S31500 00Cr18Ni5Mo3Si2 3RE60 slab ingot,S31500 00Cr18Ni5Mo3Si2 3RE60 slab,S31500 00Cr18Ni5Mo3Si2 3RE60 price,S31500 00Cr18Ni5Mo3Si2 3RE60 square bar,S31500 00Cr18Ni5Mo3Si2 3RE60 square steel,S31500 00Cr18Ni5Mo3Si2 3RE60 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of S31500 00Cr18Ni5Mo3Si2 3RE60.

Current Location:Home » Products » Stainless Steel » S31500 00Cr18Ni5Mo3Si2 3RE60

Product category

S31500 00Cr18Ni5Mo3Si2 3RE60

Data Table for:Products: Stainless Steel:S31500 00Cr18Ni5Mo3Si2 3RE60

S31500 00Cr18Ni5Mo3Si2 3RE60 properties and heat treatment forged piece, Including S31500 00Cr18Ni5Mo3Si2 3RE60 application and specifications, We have all specifications,Including S31500 00Cr18Ni5Mo3Si2 3RE60 steel plate, S31500 00Cr18Ni5Mo3Si2 3RE60 sheet, S31500 00Cr18Ni5Mo3Si2 3RE60 square steel, S31500 00Cr18Ni5Mo3Si2 3RE60 flat bar,S31500 00Cr18Ni5Mo3Si2 3RE60 round bar,S31500 00Cr18Ni5Mo3Si2 3RE60 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the S31500 00Cr18Ni5Mo3Si2 3RE60 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade S31500 00Cr18Ni5Mo3Si2 3RE60 and Standards

Step Shaft S31500 Tube S31500 Pie-shaped S31500 Ring S31500 Module S31500 Large valves of the main S31500 Other Profiled Forgings S31500

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download S31500 00Cr18Ni5Mo3Si2 3RE60 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.