Our to produce better steel-based products are the main used in industrial manufacturing various types Nickel base alloy and high nickel containing steelsNiCr20TiAl plate,NiCr20TiAl Round Bar,NiCr20TiAl forgings,NiCr20TiAl suppliers, NiCr20TiAl Stock,NiCr20TiAl sheet, NiCr20TiAl flat bar, NiCr20TiAl pipe,NiCr20TiAl tube,NiCr20TiAl mould,NiCr20TiAl round ingot,NiCr20TiAl cold-rolled steel,NiCr20TiAl coil,NiCr20TiAl strap steel,NiCr20TiAl hot-rolled steel,NiCr20TiAl medium plate, NiCr20TiAl heavy plate,NiCr20TiAl shapped bar,NiCr20TiAl hexahedral bar,NiCr20TiAl,NiCr20TiAl slab ingot,NiCr20TiAl slab,NiCr20TiAl price,NiCr20TiAl square bar,NiCr20TiAl square steel,NiCr20TiAl wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of NiCr20TiAl.

Current Location:Home » Products » Nickel base alloy and high nickel containing steels » NiCr20TiAl

Product category


Data Table for:Products: Nickel base alloy and high nickel containing steels:NiCr20TiAl

NiCr20TiAl properties and heat treatment forged piece, Including NiCr20TiAl application and specifications, We have all specifications,Including NiCr20TiAl steel plate, NiCr20TiAl sheet, NiCr20TiAl square steel, NiCr20TiAl flat bar,NiCr20TiAl round bar,NiCr20TiAl forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the NiCr20TiAl has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade NiCr20TiAl and Standards

Material number 2.4952 - NiCr20TiAl

Composition in % :

0,04 - 0,10
max. 1,00
max. 1,00
max. 0,020
max. 0,015
18,00 - 21,00
72,00 - 79,00


1,80 - 2,70
max. 0,20
1,00 - 1,80
max. 0,008
max. 1,50


Range of application and heat treatment :

Nickel alloy : components for gas turbines and transmissions , tools for hot forming
Solution annealing : 1060 - 1080 °C (air)

General and distinctive features :

Machining performance

Download NiCr20TiAl the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:NiCr20TiAl steel plate, NiCr20TiAl sheet, NiCr20TiAl square steel, NiCr20TiAl flat bar,NiCr20TiAl round bar,NiCr20TiAl forgings