Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyNiCr20Co18Ti plate,NiCr20Co18Ti Round Bar,NiCr20Co18Ti forgings,NiCr20Co18Ti suppliers, NiCr20Co18Ti Stock,NiCr20Co18Ti sheet, NiCr20Co18Ti flat bar, NiCr20Co18Ti pipe,NiCr20Co18Ti tube,NiCr20Co18Ti mould,NiCr20Co18Ti round ingot,NiCr20Co18Ti cold-rolled steel,NiCr20Co18Ti coil,NiCr20Co18Ti strap steel,NiCr20Co18Ti hot-rolled steel,NiCr20Co18Ti medium plate, NiCr20Co18Ti heavy plate,NiCr20Co18Ti shapped bar,NiCr20Co18Ti hexahedral bar,NiCr20Co18Ti,NiCr20Co18Ti slab ingot,NiCr20Co18Ti slab,NiCr20Co18Ti price,NiCr20Co18Ti square bar,NiCr20Co18Ti square steel,NiCr20Co18Ti wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of NiCr20Co18Ti.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » NiCr20Co18Ti

Product category

NiCr20Co18Ti

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:NiCr20Co18Ti

NiCr20Co18Ti properties and heat treatment forged piece, Including NiCr20Co18Ti application and specifications, We have all specifications,Including NiCr20Co18Ti steel plate, NiCr20Co18Ti sheet, NiCr20Co18Ti square steel, NiCr20Co18Ti flat bar,NiCr20Co18Ti round bar,NiCr20Co18Ti forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the NiCr20Co18Ti has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade NiCr20Co18Ti and Standards

C Si Mn P ≤ S≤ Cr Ni Mo Other
≤0.13 ≤1.00 ≤1.00 0.030 0.015 18.0-21.0    

Co 15-21.0
Al 1.00-2.00
Ti 2.0-3.0
Zr ≤0.15;B≤0.020
Fe ≤1.50;Cu≤0.20

 




Machining performance

Download NiCr20Co18Ti the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:NiCr20Co18Ti steel plate, NiCr20Co18Ti sheet, NiCr20Co18Ti square steel, NiCr20Co18Ti flat bar,NiCr20Co18Ti round bar,NiCr20Co18Ti forgings