Our to produce better steel-based products are the main used in industrial manufacturing various types Nickel base alloy and high nickel containing steelsNi36 plate,Ni36 Round Bar,Ni36 forgings,Ni36 suppliers, Ni36 Stock,Ni36 sheet, Ni36 flat bar, Ni36 pipe,Ni36 tube,Ni36 mould,Ni36 round ingot,Ni36 cold-rolled steel,Ni36 coil,Ni36 strap steel,Ni36 hot-rolled steel,Ni36 medium plate, Ni36 heavy plate,Ni36 shapped bar,Ni36 hexahedral bar,Ni36,Ni36 slab ingot,Ni36 slab,Ni36 price,Ni36 square bar,Ni36 square steel,Ni36 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ni36.

Current Location:Home » Products » Nickel base alloy and high nickel containing steels » Ni36

Product category

Ni36

Data Table for:Products: Nickel base alloy and high nickel containing steels:Ni36

Ni36 properties and heat treatment forged piece, Including Ni36 application and specifications, We have all specifications,Including Ni36 steel plate, Ni36 sheet, Ni36 square steel, Ni36 flat bar,Ni36 round bar,Ni36 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ni36 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ni36 and Standards

Material number 1.3912 - Ni36

Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
max. 0,10
max. 0,50
max. 0,50
max. 0,025
max. 0,025
max. 0,50
max. 0,50
35,0 - 37,0

 

V
W
Ti
Cu
Al
Nb
Co
Fe
 
 
 
 
 
 
max. 1,00
60,00 - 65,00




Machining performance

Download Ni36 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ni36 steel plate, Ni36 sheet, Ni36 square steel, Ni36 flat bar,Ni36 round bar,Ni36 forgings