NITRONIC 50 Stainless Steel
NITRONIC 50 Stainless Steel properties and heat treatment forged piece, Including NITRONIC 50 Stainless Steel application and specifications, We have all specifications，Including NITRONIC 50 Stainless Steel steel plate, NITRONIC 50 Stainless Steel sheet, NITRONIC 50 Stainless Steel square steel, NITRONIC 50 Stainless Steel flat bar,NITRONIC 50 Stainless Steel round bar,NITRONIC 50 Stainless Steel forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the NITRONIC 50 Stainless Steel has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade NITRONIC 50 Stainless Steel and Standards
Nitronic 50 Stainless Steel provides a combination of corrosion resistance and strength not found in any other commercial material available in its price range. This austenitic stainless steel has corrosion resistance greater than that provided by Types 316, 316L, 317 and 317L, plus approximately twice the yield strength at room temperatures. In addistion, Nitronic 50 stainless steel has very good mechanical properties at both elevated and sub-zero temperatures. Unlike many austenitic Stainless Steels, Nitronic 50 does not become magnetic when cold worked or cooled to sub-zero temperatures. High Strength (HS) Nitronic 50 stainless steel has a yield strength about three to four times that of Type 316 stainless stee.
Available Forms
Nitronic 50 stainless steel is available in bar, master alloy pigs, ingots and forging quality billets. Forms available from other manufacturers include castings, extrusions, seamless tubing and plate.
Applications Potential
Outstanding corrosion resistance gives Nitronic 50 stainless steel the leading edge for applications where Types 316, 316L, 317 and 317L are only marginal. It's an effective alloy for the petroleum, petrochemical, chemical, fertilizer, nuclear fuel recycling, pulp and paper, textile, food processing and marine industries.
Components using combination of excellent corrosion resistance and high strength currently include pumps, valves and fittings, fasteners, cables, chains, screens and wire cloth, marine hardware, boat and pump shafting, heat exchanger parts, springs and photgraphic equipment.
Machining performance
Download NITRONIC 50 Stainless Steel the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.