Our to produce better steel-based products are the main used in industrial manufacturing various types Mould steelM303 plate,M303 Round Bar,M303 forgings,M303 suppliers, M303 Stock,M303 sheet, M303 flat bar, M303 pipe,M303 tube,M303 mould,M303 round ingot,M303 cold-rolled steel,M303 coil,M303 strap steel,M303 hot-rolled steel,M303 medium plate, M303 heavy plate,M303 shapped bar,M303 hexahedral bar,M303,M303 slab ingot,M303 slab,M303 price,M303 square bar,M303 square steel,M303 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of M303.

Current Location:Home » Products » Mould steel » M303

Product category

M303

Data Table for:Products: Mould steel:M303

M303 properties and heat treatment forged piece, Including M303 application and specifications, We have all specifications,Including M303 steel plate, M303 sheet, M303 square steel, M303 flat bar,M303 round bar,M303 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the M303 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade M303 and Standards

Component Elements Properties
Metric
English
Comments
Carbon, C 
0.270 %
0.270 %
Chromium, Cr 
14.5 %
14.5 %
Iron, Fe 
82.4 %
82.4 %
As Balance
Manganese, Mn 
0.650 %
0.650 %
Molybdenum, Mo 
1.00 %
1.00 %
Nickel, Ni 
0.850 %
0.850 %
Silicon, Si 
0.300 %
0.300 %

 
 
Physical Properties
Metric
English
Comments
Density 
7.70 g/cc
0.278 lb/in³
 
Mechanical Properties
Metric
English
Comments
Hardness, Brinell 
290 - 330
290 - 330
as supplied; hardened and tempered
Hardness, Rockwell C 
53.0
53.0
hardening at 1020°C; without tempering
Modulus of Elasticity  
168 GPa
@Temperature 600 °C
24400 ksi
@Temperature 1110 °F
 
181 GPa
@Temperature 500 °C
26300 ksi
@Temperature 932 °F
 
191 GPa
@Temperature 400 °C
27700 ksi
@Temperature 752 °F
 
200 GPa
@Temperature 300 °C
29000 ksi
@Temperature 572 °F
 
207 GPa
@Temperature 200 °C
30000 ksi
@Temperature 392 °F
 
214 GPa
@Temperature 100 °C
31000 ksi
@Temperature 212 °F
 
218 GPa
@Temperature 20.0 °C
31600 ksi
@Temperature 68.0 °F



Machining performance

Download M303 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.