Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelJS-700 plate,JS-700 Round Bar,JS-700 forgings,JS-700 suppliers, JS-700 Stock,JS-700 sheet, JS-700 flat bar, JS-700 pipe,JS-700 tube,JS-700 mould,JS-700 round ingot,JS-700 cold-rolled steel,JS-700 coil,JS-700 strap steel,JS-700 hot-rolled steel,JS-700 medium plate, JS-700 heavy plate,JS-700 shapped bar,JS-700 hexahedral bar,JS-700,JS-700 slab ingot,JS-700 slab,JS-700 price,JS-700 square bar,JS-700 square steel,JS-700 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of JS-700.

Current Location:Home » Products » Stainless Steel » JS-700

Product category

JS-700

Data Table for:Products: Stainless Steel:JS-700

JS-700 properties and heat treatment forged piece, Including JS-700 application and specifications, We have all specifications,Including JS-700 steel plate, JS-700 sheet, JS-700 square steel, JS-700 flat bar,JS-700 round bar,JS-700 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the JS-700 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade JS-700 and Standards

JS-700
Category  steel
Class  Stainless steel
Type  Austenitic nonstandard

Composition
Element Weight %
C  0.04 
Mn  2.00 
Si  1.00 
Cr  19.0-23.0 
Ni  24.0-26.0 
P  0.04 
S  0.03 
Mo  43-5.0 
Cu  0.5 
Nb  0.32 (min) 
Pb  0.005 
Sn  0.035 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 550  25  annealed (plate, sheet, strip) 
Yield Strength (Mpa) 205 
Elongation (%) 30 
Reduction in Area (%) 40 




Machining performance

Download JS-700 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:JS-700 steel plate, JS-700 sheet, JS-700 square steel, JS-700 flat bar,JS-700 round bar,JS-700 forgings