Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyInconel 751 plate,Inconel 751 Round Bar,Inconel 751 forgings,Inconel 751 suppliers, Inconel 751 Stock,Inconel 751 sheet, Inconel 751 flat bar, Inconel 751 pipe,Inconel 751 tube,Inconel 751 mould,Inconel 751 round ingot,Inconel 751 cold-rolled steel,Inconel 751 coil,Inconel 751 strap steel,Inconel 751 hot-rolled steel,Inconel 751 medium plate, Inconel 751 heavy plate,Inconel 751 shapped bar,Inconel 751 hexahedral bar,Inconel 751,Inconel 751 slab ingot,Inconel 751 slab,Inconel 751 price,Inconel 751 square bar,Inconel 751 square steel,Inconel 751 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Inconel 751.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Inconel 751

Product category

Inconel 751

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Inconel 751

Inconel 751 properties and heat treatment forged piece, Including Inconel 751 application and specifications, We have all specifications,Including Inconel 751 steel plate, Inconel 751 sheet, Inconel 751 square steel, Inconel 751 flat bar,Inconel 751 round bar,Inconel 751 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Inconel 751 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Inconel 751 and Standards

Principal Design Features
This alloy is a slightly modified chemistry version of Inconel X-750. The aluminum content has been increased in order to impart improved rupture strength in the 1600 F range.

request for quote

Applications
Applications are those where hot strength in the 1600 F range is of major importance. One such specific use is for exhaust valves on heavy duty diesel engines.

Machinability
Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting.
 




Machining performance

Download Inconel 751 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.