Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyInconel 601 plate,Inconel 601 Round Bar,Inconel 601 forgings,Inconel 601 suppliers, Inconel 601 Stock,Inconel 601 sheet, Inconel 601 flat bar, Inconel 601 pipe,Inconel 601 tube,Inconel 601 mould,Inconel 601 round ingot,Inconel 601 cold-rolled steel,Inconel 601 coil,Inconel 601 strap steel,Inconel 601 hot-rolled steel,Inconel 601 medium plate, Inconel 601 heavy plate,Inconel 601 shapped bar,Inconel 601 hexahedral bar,Inconel 601,Inconel 601 slab ingot,Inconel 601 slab,Inconel 601 price,Inconel 601 square bar,Inconel 601 square steel,Inconel 601 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Inconel 601.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Inconel 601

Product category

Inconel 601

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Inconel 601

Inconel 601 properties and heat treatment forged piece, Including Inconel 601 application and specifications, We have all specifications,Including Inconel 601 steel plate, Inconel 601 sheet, Inconel 601 square steel, Inconel 601 flat bar,Inconel 601 round bar,Inconel 601 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Inconel 601 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Inconel 601 and Standards

Principal Design Features
A nickel-chromium-iron alloy with excellent resistance to high temperature oxidation. A general purpose material for applications where heat and corrosion resistance are the primary considerations.

request for quote

Applications
A construction alloy for heat treat furnace fixtures and components such as annealing tubes, muffles, flame shields. Also useful for chemical process equipment such as combustor components, process heaters, and condenser tubes.

Machinability
Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting. Most any commercial coolant may be used in the machining operations. Water-base coolants are preferred for high speed operations such as turning, grinding, or milling. Heavy lubricants work best for drilling, tapping, broaching or boring.
 




Machining performance

Download Inconel 601 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.