Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelICI 8620 plate,ICI 8620 Round Bar,ICI 8620 forgings,ICI 8620 suppliers, ICI 8620 Stock,ICI 8620 sheet, ICI 8620 flat bar, ICI 8620 pipe,ICI 8620 tube,ICI 8620 mould,ICI 8620 round ingot,ICI 8620 cold-rolled steel,ICI 8620 coil,ICI 8620 strap steel,ICI 8620 hot-rolled steel,ICI 8620 medium plate, ICI 8620 heavy plate,ICI 8620 shapped bar,ICI 8620 hexahedral bar,ICI 8620,ICI 8620 slab ingot,ICI 8620 slab,ICI 8620 price,ICI 8620 square bar,ICI 8620 square steel,ICI 8620 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ICI 8620.

Current Location:Home » Products » Alloy steel » ICI 8620

Product category

ICI 8620

Data Table for:Products: Alloy steel:ICI 8620

ICI 8620 properties and heat treatment forged piece, Including ICI 8620 application and specifications, We have all specifications,Including ICI 8620 steel plate, ICI 8620 sheet, ICI 8620 square steel, ICI 8620 flat bar,ICI 8620 round bar,ICI 8620 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ICI 8620 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ICI 8620 and Standards

C
Si
Mn
P
S
Cr Ni
0.15-0.25 0.2-0.8 0.65-0.95 0.04 0.045 0.4-0.7 0.4-0.7
Mo Al Cu Nb Ti W V
0.15-0.25   0.5     0.1  




Machining performance

Download ICI 8620 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.