Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelHigh Speed Steel Tool Bits plate,High Speed Steel Tool Bits Round Bar,High Speed Steel Tool Bits forgings,High Speed Steel Tool Bits suppliers, High Speed Steel Tool Bits Stock,High Speed Steel Tool Bits sheet, High Speed Steel Tool Bits flat bar, High Speed Steel Tool Bits pipe,High Speed Steel Tool Bits tube,High Speed Steel Tool Bits mould,High Speed Steel Tool Bits round ingot,High Speed Steel Tool Bits cold-rolled steel,High Speed Steel Tool Bits coil,High Speed Steel Tool Bits strap steel,High Speed Steel Tool Bits hot-rolled steel,High Speed Steel Tool Bits medium plate, High Speed Steel Tool Bits heavy plate,High Speed Steel Tool Bits shapped bar,High Speed Steel Tool Bits hexahedral bar,High Speed Steel Tool Bits,High Speed Steel Tool Bits slab ingot,High Speed Steel Tool Bits slab,High Speed Steel Tool Bits price,High Speed Steel Tool Bits square bar,High Speed Steel Tool Bits square steel,High Speed Steel Tool Bits wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of High Speed Steel Tool Bits.

Current Location:Home » Products » Stainless Steel » High Speed Steel Tool Bits

Product category

High Speed Steel Tool Bits

Data Table for:Products: Stainless Steel:High Speed Steel Tool Bits

High Speed Steel Tool Bits properties and heat treatment forged piece, Including High Speed Steel Tool Bits application and specifications, We have all specifications,Including High Speed Steel Tool Bits steel plate, High Speed Steel Tool Bits sheet, High Speed Steel Tool Bits square steel, High Speed Steel Tool Bits flat bar,High Speed Steel Tool Bits round bar,High Speed Steel Tool Bits forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the High Speed Steel Tool Bits has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade High Speed Steel Tool Bits and Standards

High Speed Steel Toolbits are available in grades M2 and M42. Listed below are our standard stock sizes. Non standard sizes in tool bits can be produced to your requirements.

  
 

TYPICAL ANALYSIS

M2 ToolBits

 

C.

Cr.

Mo.

W.

V.

0.85%

4.0%

5.0%

6.0%

2.0%

   

TYPICALANALYSIS

 M42ToolBits 

 

 

C.

Cr.

Mo.

W.

V.

Co.

1.05%

3.9%

9.5%

1.5%

1.15%

8.0%

 

Squares
supplied with bevelled ends

Rounds
supplied with square ends

Rectangular
supplied with square ends

3/16" sq x 2 1/2"

3/16" dia x 2 1/2"

1/2" x 3/8" x 4"

3/16" sq x 3"

3/16" dia x 3"

5/8" x 3/8" x 4"

3/16" sq x 4"

3/16" dia x 4"

3/4" x 1/2" x 4"

1/4" sq x 2 1/2"

1/4" dia x 2 1/2"

1" x 1/2" x 6"

1/4" sq x 3"

1/4" dia x 3"

1" x 5/8" x 6"

1/4" sq x 4"

1/4" dia x 4"

1" x 3/4" x 6"

5/16" sq x 3"

5/16" dia x 3"

1 1/2" x 1/2" x 6"

5/16" sq x 4"

5/16" dia x 4"

1 3/8" x 1/2" x 6"

3/8" sq x 3"

3/8" dia x 3"

1 1/4" x 1/2" x 4"

3/8" sq x 4"

3/8" dia x 4"

1 1/4" x 1/2" x 6"

3/8" sq x 6"

3/8" dia x 6"

1 1/4" x 3/8" x 4"

1/2" sq x 3"

1/2" dia x 3"

1 1/4" x 3/8" x 6"

1/2" sq x 4"

1/2" dia x 4"

1" x 3/8" x 6"

1/2" sq x 6"

1/2" dia x 6"

1" x 3/8" x 8"

5/8" sq x 4"

5/8" dia x 4"

1" x 1/4" x 6"

5/8" sq x 6"

5/8" dia x 6"

1" x 1/4" x 8"

3/4" sq x 4"

3/4" dia x 4"

3/4" sq x 6"

3/4" dia x 6"

1" sq x 6" 

1" dia x 6"

For price and availability on tool bits contact our friendly and helpful staff.



Machining performance

Download High Speed Steel Tool Bits the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:High Speed Steel Tool Bits steel plate, High Speed Steel Tool Bits sheet, High Speed Steel Tool Bits square steel, High Speed Steel Tool Bits flat bar,High Speed Steel Tool Bits round bar,High Speed Steel Tool Bits forgings