Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyHastelloy C plate,Hastelloy C Round Bar,Hastelloy C forgings,Hastelloy C suppliers, Hastelloy C Stock,Hastelloy C sheet, Hastelloy C flat bar, Hastelloy C pipe,Hastelloy C tube,Hastelloy C mould,Hastelloy C round ingot,Hastelloy C cold-rolled steel,Hastelloy C coil,Hastelloy C strap steel,Hastelloy C hot-rolled steel,Hastelloy C medium plate, Hastelloy C heavy plate,Hastelloy C shapped bar,Hastelloy C hexahedral bar,Hastelloy C,Hastelloy C slab ingot,Hastelloy C slab,Hastelloy C price,Hastelloy C square bar,Hastelloy C square steel,Hastelloy C wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Hastelloy C.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Hastelloy C

Product category

Hastelloy C

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Hastelloy C

Hastelloy C properties and heat treatment forged piece, Including Hastelloy C application and specifications, We have all specifications,Including Hastelloy C steel plate, Hastelloy C sheet, Hastelloy C square steel, Hastelloy C flat bar,Hastelloy C round bar,Hastelloy C forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Hastelloy C has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Hastelloy C and Standards

General Characteristics of Hastelloy C™
An alloy composed of nickel, molybdenum, chromium and iron, Hastelloy™ Alloy-C maintains its outstanding properties in extreme heat, holding its strength and resisting oxidation. The alloy also resists chlorine and compounds with chlorine, as well as strong oxidizing acids, acid mixes and salts. One of the most corrosion-resistant alloys, it’s exceptional in high-stress applications and in environments prone to repeated thermal shock.

Chemical Composition of Hastelloy C™
Carbon 0.15 max
Tungsten 3.75-5.25
Iron 4.5-7.0
Chromium 15.5-17.5
Molybdenum 16.0-18.0
Vanadium 0.20-0.40
Manganese 1.0 max
Silicon 1.0 max
Phosphorus 0.04 max
Sulfur 0.03 max
Nickel remainder
Heat Treatment of Hastelloy C™
Anneal: Heat at 2235=20 deg F for a length of time dedicated by the mass and cross section. Air cool generally to 1 to 2 hours.
Age hardening after annealing:
Hold at 1575°-1600°F (857°-871°C) for 8-10 hours
Air-cool to Rockwell C 35-40
Hold castings for 16 hours at aging temperature to achieve hardness and high yield strength (not required or suggested to resist corrosion on for strength at high temperatures).
Applications of Hastelloy C™
Combustion chambers
Heat-treating equipment
Collector rings, combustion chambers and exhaust stacks for high-heat applications in for conventional aircraft and jets
Pipe connections, pumps and valves for oil refinery, chemical and petrochemical applications
Machinability of Hastelloy C™
Can be machined at low cutting speeds
Use sintered carbide cutting tools and grind to 6-7 degree side clearance and 10-15 degree side rake angle for facing or turning operations
Use short drill and grind with minimum clearance to clear the work – generally about 140 degrees total – when drilling
Use sulfur-based oil coolant when drilling, or when turning, facing, or boring at higher speeds
Workability of Hastelloy C™
Preheat to temperatures to 2200°-2250° F (1204°-1232°C)
Forge with hot working p




Machining performance

Download Hastelloy C the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.