Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyHastelloy B2 plate,Hastelloy B2 Round Bar,Hastelloy B2 forgings,Hastelloy B2 suppliers, Hastelloy B2 Stock,Hastelloy B2 sheet, Hastelloy B2 flat bar, Hastelloy B2 pipe,Hastelloy B2 tube,Hastelloy B2 mould,Hastelloy B2 round ingot,Hastelloy B2 cold-rolled steel,Hastelloy B2 coil,Hastelloy B2 strap steel,Hastelloy B2 hot-rolled steel,Hastelloy B2 medium plate, Hastelloy B2 heavy plate,Hastelloy B2 shapped bar,Hastelloy B2 hexahedral bar,Hastelloy B2,Hastelloy B2 slab ingot,Hastelloy B2 slab,Hastelloy B2 price,Hastelloy B2 square bar,Hastelloy B2 square steel,Hastelloy B2 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Hastelloy B2.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Hastelloy B2

Product category

Hastelloy B2

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Hastelloy B2

Hastelloy B2 properties and heat treatment forged piece, Including Hastelloy B2 application and specifications, We have all specifications,Including Hastelloy B2 steel plate, Hastelloy B2 sheet, Hastelloy B2 square steel, Hastelloy B2 flat bar,Hastelloy B2 round bar,Hastelloy B2 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Hastelloy B2 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Hastelloy B2 and Standards

Principal Design Features
A wrought nickel-molybdenum alloy that can be used in the as welded condition. It is highly resistant to all concentrations and temperatures of hydrochloric acid. Also resistant to stress corrosion cracking and pitting.




Machining performance

Download Hastelloy B2 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.