Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelDIN 1.4303 plate,DIN 1.4303 Round Bar,DIN 1.4303 forgings,DIN 1.4303 suppliers, DIN 1.4303 Stock,DIN 1.4303 sheet, DIN 1.4303 flat bar, DIN 1.4303 pipe,DIN 1.4303 tube,DIN 1.4303 mould,DIN 1.4303 round ingot,DIN 1.4303 cold-rolled steel,DIN 1.4303 coil,DIN 1.4303 strap steel,DIN 1.4303 hot-rolled steel,DIN 1.4303 medium plate, DIN 1.4303 heavy plate,DIN 1.4303 shapped bar,DIN 1.4303 hexahedral bar,DIN 1.4303,DIN 1.4303 slab ingot,DIN 1.4303 slab,DIN 1.4303 price,DIN 1.4303 square bar,DIN 1.4303 square steel,DIN 1.4303 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of DIN 1.4303.

Current Location:Home » Products » Stainless Steel » DIN 1.4303

Product category

DIN 1.4303

Data Table for:Products: Stainless Steel:DIN 1.4303

DIN 1.4303 properties and heat treatment forged piece, Including DIN 1.4303 application and specifications, We have all specifications,Including DIN 1.4303 steel plate, DIN 1.4303 sheet, DIN 1.4303 square steel, DIN 1.4303 flat bar,DIN 1.4303 round bar,DIN 1.4303 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the DIN 1.4303 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade DIN 1.4303 and Standards

Category  steel
Class  Stainless steel
Type  Austenitic standard
Common Names  Chromium-Nickel steel
Designations  Germany: DIN 1.4303
Italy: UNI X 8 CrNi 19 10
Japan: JIS SUS 305 , JIS SUS 305 J1
United States: AMS 5514 , AMS 5685 , AMS 5686 , ASME SA193 , ASME SA194 , ASME SA240 , ASTM A167 , ASTM A240 , ASTM A249 , ASTM A276 , ASTM A313 , ASTM A314 , ASTM A368 , ASTM A473 , ASTM A478 , ASTM A492 , ASTM A493 , ASTM A511 , ASTM A554 , ASTM A580 , FED QQ-S-763 , FED QQ-W-423 , SAE 30305 , SAE J405 (30305) , UNS S30500

Composition
Element Weight %
C  0.12 
Mn  2.00 
Si  1.00 
Cr  17.0-19.0 
Ni  10.5-13.0 
P  0.045 
S  0.03 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 8 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 193 25  
Tensile Strength (Mpa) 515  25  hot finished and annealed (plate, sheet, strip) more
Yield Strength (Mpa) 205 
Elongation (%) 40 
Reduction in Area (%) 50 
Hardness (HRB) 88 (max)  25  annealed (plate, sheet, strip) 

Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 17.2  0-100 more  
Thermal Conductivity (W/m-K) 16.2  100 more  
Specific Heat (J/kg-K) 500  0-100   

Electric Properties
Properties  Conditions 
T (°C) Treatment
Electric Resistivity (10-9W-m) 720  25   




Machining performance

Download DIN 1.4303 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:DIN 1.4303 steel plate, DIN 1.4303 sheet, DIN 1.4303 square steel, DIN 1.4303 flat bar,DIN 1.4303 round bar,DIN 1.4303 forgings