Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelDIN 1.2330 plate,DIN 1.2330 Round Bar,DIN 1.2330 forgings,DIN 1.2330 suppliers, DIN 1.2330 Stock,DIN 1.2330 sheet, DIN 1.2330 flat bar, DIN 1.2330 pipe,DIN 1.2330 tube,DIN 1.2330 mould,DIN 1.2330 round ingot,DIN 1.2330 cold-rolled steel,DIN 1.2330 coil,DIN 1.2330 strap steel,DIN 1.2330 hot-rolled steel,DIN 1.2330 medium plate, DIN 1.2330 heavy plate,DIN 1.2330 shapped bar,DIN 1.2330 hexahedral bar,DIN 1.2330,DIN 1.2330 slab ingot,DIN 1.2330 slab,DIN 1.2330 price,DIN 1.2330 square bar,DIN 1.2330 square steel,DIN 1.2330 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of DIN 1.2330.

Current Location:Home » Products » Stainless Steel » DIN 1.2330

Product category

DIN 1.2330

Data Table for:Products: Stainless Steel:DIN 1.2330

DIN 1.2330 properties and heat treatment forged piece, Including DIN 1.2330 application and specifications, We have all specifications,Including DIN 1.2330 steel plate, DIN 1.2330 sheet, DIN 1.2330 square steel, DIN 1.2330 flat bar,DIN 1.2330 round bar,DIN 1.2330 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the DIN 1.2330 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade DIN 1.2330 and Standards

Category  steel
Class  Tool steel
Type  General mold steel
Designations  Germany: DIN 1.2330
United States: ASTM A681 , UNS T51620

Composition
Element Weight %
C  0.28-0.40 
Mn  0.60-1.00 
Si  0.20-0.80 
Cr  1.40-2.00 
Mo  0.30-0.55 
Cu  0.25 
P  0.03 
S  0.03 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.85 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  

Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 12.8  20-425 more  




Machining performance

Download DIN 1.2330 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.