Our to produce better steel-based products are the main used in industrial manufacturing various types Cementation steelsC15E2C plate,C15E2C Round Bar,C15E2C forgings,C15E2C suppliers, C15E2C Stock,C15E2C sheet, C15E2C flat bar, C15E2C pipe,C15E2C tube,C15E2C mould,C15E2C round ingot,C15E2C cold-rolled steel,C15E2C coil,C15E2C strap steel,C15E2C hot-rolled steel,C15E2C medium plate, C15E2C heavy plate,C15E2C shapped bar,C15E2C hexahedral bar,C15E2C,C15E2C slab ingot,C15E2C slab,C15E2C price,C15E2C square bar,C15E2C square steel,C15E2C wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of C15E2C.

Current Location:Home » Products » Cementation steels » C15E2C

Product category

C15E2C

Data Table for:Products: Cementation steels:C15E2C

C15E2C properties and heat treatment forged piece, Including C15E2C application and specifications, We have all specifications,Including C15E2C steel plate, C15E2C sheet, C15E2C square steel, C15E2C flat bar,C15E2C round bar,C15E2C forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the C15E2C has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade C15E2C and Standards

Material number 1.1132 - CQ15 / C15C / C15E2C

Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
0,12 - 0,18
0,15 - 0,35
0,25 - 0,50
max. 0,035
max. 0,035
 
 
 

 

V

 
W
Ti
Cu
Al
Nb
B
N
 
 
 
 
 
 
 

 

Range of application and heat treatment :

Cold extrusion steel : universal machines- , engines- and vehicle engineering
Hardening : 880 - 920 °C (water) Soft annealing : 650 - 700 °C Normalising : 880 - 920 °C
 

General and distinctive features :

 




Machining performance

Download C15E2C the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.