Our to produce better steel-based products are the main used in industrial manufacturing various types Cementation steelsC10C plate,C10C Round Bar,C10C forgings,C10C suppliers, C10C Stock,C10C sheet, C10C flat bar, C10C pipe,C10C tube,C10C mould,C10C round ingot,C10C cold-rolled steel,C10C coil,C10C strap steel,C10C hot-rolled steel,C10C medium plate, C10C heavy plate,C10C shapped bar,C10C hexahedral bar,C10C,C10C slab ingot,C10C slab,C10C price,C10C square bar,C10C square steel,C10C wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of C10C.

Current Location:Home » Products » Cementation steels » C10C

Product category

C10C

Data Table for:Products: Cementation steels:C10C

C10C properties and heat treatment forged piece, Including C10C application and specifications, We have all specifications,Including C10C steel plate, C10C sheet, C10C square steel, C10C flat bar,C10C round bar,C10C forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the C10C has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade C10C and Standards

Material number 1.1122 - CQ10 / C10C / C10E2C

Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
0,07 - 0,13
0,15 - 0,35
0,25 - 0,50
max. 0,035
max. 0,035
 
 
 

 
 

V
W
Ti
Cu
Al
Nb
B
N
 
 
 
 
 
 
 
 

Range of application and heat treatment :

Cold extrusion steel : universal machines- , engines- and vehicle engineering
Hardening : 880 - 920 °C (water) Soft annealing : 650 - 700 °C Normalising : 880 - 920 °C
 

General and distinctive features :




Machining performance

Download C10C the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:C10C steel plate, C10C sheet, C10C square steel, C10C flat bar,C10C round bar,C10C forgings