Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelASTM M50 plate,ASTM M50 Round Bar,ASTM M50 forgings,ASTM M50 suppliers, ASTM M50 Stock,ASTM M50 sheet, ASTM M50 flat bar, ASTM M50 pipe,ASTM M50 tube,ASTM M50 mould,ASTM M50 round ingot,ASTM M50 cold-rolled steel,ASTM M50 coil,ASTM M50 strap steel,ASTM M50 hot-rolled steel,ASTM M50 medium plate, ASTM M50 heavy plate,ASTM M50 shapped bar,ASTM M50 hexahedral bar,ASTM M50,ASTM M50 slab ingot,ASTM M50 slab,ASTM M50 price,ASTM M50 square bar,ASTM M50 square steel,ASTM M50 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM M50.

Current Location:Home » Products » Tool steel » ASTM M50

Product category

ASTM M50

Data Table for:Products: Tool steel:ASTM M50

ASTM M50 properties and heat treatment forged piece, Including ASTM M50 application and specifications, We have all specifications,Including ASTM M50 steel plate, ASTM M50 sheet, ASTM M50 square steel, ASTM M50 flat bar,ASTM M50 round bar,ASTM M50 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM M50 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM M50 and Standards

C
Si
Mn
P
S
Cr Ni
0.78-0.88 0.2-0.6 0.15-0.45 0.03 0.03 3.75-4.5  
Mo Al W Nb Ti V Ce
3.9-4.75         0.8-1.25  




Machining performance

Download ASTM M50 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.