Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM A743M plate,ASTM A743M Round Bar,ASTM A743M forgings,ASTM A743M suppliers, ASTM A743M Stock,ASTM A743M sheet, ASTM A743M flat bar, ASTM A743M pipe,ASTM A743M tube,ASTM A743M mould,ASTM A743M round ingot,ASTM A743M cold-rolled steel,ASTM A743M coil,ASTM A743M strap steel,ASTM A743M hot-rolled steel,ASTM A743M medium plate, ASTM A743M heavy plate,ASTM A743M shapped bar,ASTM A743M hexahedral bar,ASTM A743M,ASTM A743M slab ingot,ASTM A743M slab,ASTM A743M price,ASTM A743M square bar,ASTM A743M square steel,ASTM A743M wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A743M.

Current Location:Home » Products » Stainless Steel » ASTM A743M

Product category

ASTM A743M

Data Table for:Products: Stainless Steel:ASTM A743M

ASTM A743M properties and heat treatment forged piece, Including ASTM A743M application and specifications, We have all specifications,Including ASTM A743M steel plate, ASTM A743M sheet, ASTM A743M square steel, ASTM A743M flat bar,ASTM A743M round bar,ASTM A743M forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A743M has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A743M and Standards

ASTM A743/A743M(98) (CA15)

Categories: Metal; Ferrous Metal; ASTM Steel; Stainless steel; Cast Stainless Steel

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  >= 620 MPa >= 89900 psi
Tensile Strength, Yield  >= 450 MPa >= 65300 psi
Elongation at Break  >= 18.0 % >= 18.0 %
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.15 % <= 0.15 %
Chromium, Cr  11.5 - 14.0 % 11.5 - 14.0 %
Iron, Fe  81.8 - 88.5 % 81.8 - 88.5 % As remainder
Manganese, Mn  <= 1.0 % <= 1.0 %
Molybdenum, Mo  <= 0.50 % <= 0.50 %
Nickel, Ni  <= 1.0 % <= 1.0 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Silicon, Si  <= 1.50 % <= 1.50 %
Sulfur, S  <= 0.040 % <= 0.040 %

Users viewing this material also viewed the following:
ASTM A487 (CA15)
ASTM A743/A743M(98) (CA6NM)
ASTM A743/A743M(98) (CA15M)
ASTM A743/A 743M98 (CA40)
ASTM A743/A743M(98) (CF8M)

MQCCA15B20 / 13331
 




Machining performance

Download ASTM A743M the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM A743M steel plate, ASTM A743M sheet, ASTM A743M square steel, ASTM A743M flat bar,ASTM A743M round bar,ASTM A743M forgings