Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM A276 plate,ASTM A276 Round Bar,ASTM A276 forgings,ASTM A276 suppliers, ASTM A276 Stock,ASTM A276 sheet, ASTM A276 flat bar, ASTM A276 pipe,ASTM A276 tube,ASTM A276 mould,ASTM A276 round ingot,ASTM A276 cold-rolled steel,ASTM A276 coil,ASTM A276 strap steel,ASTM A276 hot-rolled steel,ASTM A276 medium plate, ASTM A276 heavy plate,ASTM A276 shapped bar,ASTM A276 hexahedral bar,ASTM A276,ASTM A276 slab ingot,ASTM A276 slab,ASTM A276 price,ASTM A276 square bar,ASTM A276 square steel,ASTM A276 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A276.

Current Location:Home » Products » Stainless Steel » ASTM A276

Product category

ASTM A276

Data Table for:Products: Stainless Steel:ASTM A276

ASTM A276 properties and heat treatment forged piece, Including ASTM A276 application and specifications, We have all specifications,Including ASTM A276 steel plate, ASTM A276 sheet, ASTM A276 square steel, ASTM A276 flat bar,ASTM A276 round bar,ASTM A276 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A276 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A276 and Standards

ASTM A276-000 (440A) Hot Formed, Annealed
Categories: Metal; Ferrous Metal; ASTM Steel; Stainless steel; Cast Stainless Steel

Mechanical Properties Metric English Comments
Hardness, Brinell  <= 269 <= 269
 
Component Elements Properties Metric English Comments
Carbon, C  0.60 - 0.75 % 0.60 - 0.75 %
Chromium, Cr  16.0 - 18.0 % 16.0 - 18.0 %
Iron, Fe  78.4 - 83.4 % 78.4 - 83.4 % As remainder
Manganese, Mn  <= 1.0 % <= 1.0 %
Molybdenum, Mo  <= 0.75 % <= 0.75 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Silicon, Si  <= 1.0 % <= 1.0 %
Sulfur, S  <= 0.030 % <= 0.030 %

Users viewing this material also viewed the following:
ASTM A276-001 (440A) Cold Rolled, Annealed
AISI 440 Stainless Steel
ASTM A487 (CA15)
Overview of materials for Cast Stainless Steel
ASTM A743/A743M(98) (CA15)

MQC440A020 / 13302
 




Machining performance

Download ASTM A276 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.