Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI Type 418 plate,AISI Type 418 Round Bar,AISI Type 418 forgings,AISI Type 418 suppliers, AISI Type 418 Stock,AISI Type 418 sheet, AISI Type 418 flat bar, AISI Type 418 pipe,AISI Type 418 tube,AISI Type 418 mould,AISI Type 418 round ingot,AISI Type 418 cold-rolled steel,AISI Type 418 coil,AISI Type 418 strap steel,AISI Type 418 hot-rolled steel,AISI Type 418 medium plate, AISI Type 418 heavy plate,AISI Type 418 shapped bar,AISI Type 418 hexahedral bar,AISI Type 418,AISI Type 418 slab ingot,AISI Type 418 slab,AISI Type 418 price,AISI Type 418 square bar,AISI Type 418 square steel,AISI Type 418 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI Type 418.

Current Location:Home » Products » Stainless Steel » AISI Type 418

Product category

AISI Type 418

Data Table for:Products: Stainless Steel:AISI Type 418

AISI Type 418 properties and heat treatment forged piece, Including AISI Type 418 application and specifications, We have all specifications,Including AISI Type 418 steel plate, AISI Type 418 sheet, AISI Type 418 square steel, AISI Type 418 flat bar,AISI Type 418 round bar,AISI Type 418 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI Type 418 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI Type 418 and Standards

Category  steel
Class  Stainless steel
Type  Martensitic standard
Common Names  Chromium steel
Designations  United States: SAE 51418

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1450  25  tempered at 260°C (bar) more
Yield Strength (Mpa) 1210 
Elongation (%) 18 
Reduction in Area (%) 52 



Machining performance

Download AISI Type 418 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.