Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 422 plate,AISI 422 Round Bar,AISI 422 forgings,AISI 422 suppliers, AISI 422 Stock,AISI 422 sheet, AISI 422 flat bar, AISI 422 pipe,AISI 422 tube,AISI 422 mould,AISI 422 round ingot,AISI 422 cold-rolled steel,AISI 422 coil,AISI 422 strap steel,AISI 422 hot-rolled steel,AISI 422 medium plate, AISI 422 heavy plate,AISI 422 shapped bar,AISI 422 hexahedral bar,AISI 422,AISI 422 slab ingot,AISI 422 slab,AISI 422 price,AISI 422 square bar,AISI 422 square steel,AISI 422 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 422.

Current Location:Home » Products » Stainless Steel » AISI 422

Product category

AISI 422

Data Table for:Products: Stainless Steel:AISI 422

AISI 422 properties and heat treatment forged piece, Including AISI 422 application and specifications, We have all specifications,Including AISI 422 steel plate, AISI 422 sheet, AISI 422 square steel, AISI 422 flat bar,AISI 422 round bar,AISI 422 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 422 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 422 and Standards

 

Designations
Germany: DIN 1.4935 
Japan: JIS SUN 616 
United States: AMS 5655 , ASTM A565 , SAE 51422 , SAE J467 , UNS S42200

 Chemical Composition
Element
Weight %
C
 0.20-0.25 
Mn
 1.00 
Si
 0.75 
Cr
 11.0-13.0 
Ni
 0.5-1.0 
P
 0.025 
S
 0.025 
Mo
 0.75-1.25 
W
 0.75-1.25 
V
 0.15-0.3 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.8
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Tensile Strength (Mpa)
965 
25 
intermediate and hard tempers (bar) 
Yield Strength (Mpa)
760 
Elongation (%)
13 
Reduction in Area (%)
30 
Thermal Properties
Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
11.2 
0-100 more
 
Thermal Conductivity (W/m-K)
23.9 
100 more
 
Specific Heat (J/kg-K)
460 
0-100 
 



Machining performance

Download AISI 422 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.